Influence of Co Content and Chemical Nature of the Co Binder on the Corrosion Resistance of Nanostructured WC-Co Hardmetals in Acidic Solution.

The electrochemical corrosion resistance of nanostructured hardmetals with grain sizes < 200 nm was researched concerning Co content and the chemical nature of the Co binder. Fully dense nanostructured hardmetals with the addition of grain growth inhibitors GGIs, VC and CrC, and 5 wt.%Co, 10 wt.%Co, and 15 wt.%Co were developed by a one cycle sinter-HIP process. The samples were detailly characterized in terms of microstructural characteristics and researched in the solution of HSO + CO by direct and alternative current techniques, including electrochemical impedance spectroscopy. Performed analysis revealed a homogeneous microstructure of equal and uniform grain size for different Co contents. The importance of GGIs content adjustment was established as a key factor of obtaining a homogeneous microstructure with WC grain size retained at the same values as in starting mixtures of different Co binder content. From the conducted research, Co content has shown to be the dominant influential factor governing electrochemical corrosion resistance of nanostructured hardmetals compared to the chemical composition of the Co binder and WC grain size. Negative values of measured for 30 min in 96% HSO + CO were obtained for all samples indicating material dissolution and instability in acidic solution. Higher values of and lower values of and were obtained for samples with lower Co content. In contrast, the anodic Tafel slope increases with increasing Co content which could be attributed to more pronounced oxidation of the higher Co content samples. Previously researched samples with the same composition but different chemical composition of the binder were introduced in the analysis. The chemical composition of the Co binder showed an influence; samples with lower relative magnetic saturation related to lower C content added to the starting mixtures and more W dissolved in the Co binder during the sintering process showed better corrosion resistance. WC-5Co sample with significantly lower magnetic saturation value showed approximately 30% lower corrosion rate. WC-10Co sample with slightly lower relative magnetic saturation value and showed approximately 10% lower corrosion rate. Higher content of CrC dissolved in the binder contributed to a lower corrosion rate. Slight VC increase did not contribute to corrosion resistance. Superior corrosion resistance is attributed to W and C dissolved in the Co binder, lower magnetic saturation, or WC grain size of the sintered sample.