Separation of ethylene-norbornene copolymers using high performance liquid chromatography.

The elution behavior of ethylene-norbornene (EN) copolymers prepared with various catalysts was studied in selected binary solvent gradients using porous graphite (Hypercarb) as stationary phase. It was found that the elution volumes of the EN copolymers correlated with their average norbornene content. For a series with norbornene content lower than 20 mol % the correlation was positive (i.e. increasing elution volumes with increasing norbornene content), whereas for a series with norbornene contents above 20 mol % it was negative (decreasing elution volumes with increasing norbornene content). It is known that EN copolymers have complicated microstructures that depend on norbornene content and the catalyst system used for synthesis. Thus, it is supposed that the opposing trends in the elution behavior of the EN copolymers are caused by differences in their microstructure, ultimately governed by the norbornene content. Our conclusions are supported by results from NMR spectroscopy, which revealed the microstructure, and differential scanning calorimetry (DSC).