Construction of wood-based cellulose micro-framework composite form-stable multifunctional materials with thermal and electrical response via incorporating erythritol-urea (thiourea)-carbon nanotubes.

In this study, two kinds of form-stable multifunctional materials with thermal and electrical response (FPCMs: DP-E7U3-CNT, DP-E7T3-CNT) are composed of wood-based honeycomb-like celluloses micro-framework (DP), carbon nanotubes (CNT), erythritol-urea (E7U3) or erythritol-thiourea (E7T3). In FPCMs, DP acts as a skeleton structure to seal E7U3 and E7T3 and provide more pathways for heat conduction. The CNT acts as an extended surface to further improve thermal conductivity. FE-SEM showed that the honeycomb-like pore structure of DP was completely filled with E7U3, E7T3 and CNT. FTIR and XRD analysis show that there is only a combination of physical interactions between the components of FPCMs. DSC curves and thermal conductivity analysis results show that DP-E7U3-1.5CNT and DP-E7T3-1.5CNT with the mass fraction of carbon nanotubes (1.5 wt%) have the highest latent heat values (230.3 J/g, 272.2 J/g) and thermal conductivity (0.9832 W/(m·K), 0.9363 W/(m·K)). Both DP-E7U3-1.5CNT and DP-E7T3-1.5CNT exhibit high latent heat retention and thermal stability after 100 heating-cooling cycles. In addition, DP-E7U3-1.5CNT and DP-E7T3-1.5CNT show excellent performance in light-heat energy conversion-storage, actual latent heat storage and release, thermal and electrical response performance, which make it has great potential to be multifunctional materials with thermal storage sand electrical response.