TiO/CTS/ATP adsorbent modification and its application in adsorption-ultrafiltration process for dye wastewater purification.

Industrial dyeing produces highly polluting wastewater and threatens the environment. Effective treatment of dyeing wastewater is a crucial step to prevent toxic chemicals from entering receiving waters. This study aimed to assess a modified attapulgite (ATP)-based adsorbent for dyeing wastewater purification by introducing chitosan (CTS) and titanium dioxide (TiO) into the adsorbent material named TiO/CTS/ATP. It was found that after modification, the adsorbent showed a lower hydrophilicity, as demonstrated by an increase in the water contact angle from 9.1° to 42°, which could reduce the water adsorption tendency and potentially facilitate contaminants adherence. The modification also led to a significantly increased specific surface area of 79.111 m/g from 3.791 m/g and exhibited more uniform and smaller particle size (reduced from 3.99 to 2.52 μm). When the TiO/CTS/ATP adsorbent was applied to the adsorption of Congo red solution, the adsorption efficiency was observed to reach to 97.6% at the dosage of 0.5 g/L. Furthermore, the combination of adsorption and ultrafiltration was able to achieve 99% Congo red removal. Adsorption pretreatment prior to the ultrafiltration also enabled to reduce membrane fouling, increased the reversible membrane fouling, and resulted in a considerably lower transmembrane pressure as compared with the direct ultrafiltration filtration system.