FeVO Nanopolyhedron Photoelectrodes for Stable and Efficient Water Splitting.

Crystalline FeVO nanopolyhedron (FVO NPH) photoelectrodes are successfully prepared by using an in situ solid-state transformation from hydrothermal FeOOH films via adding vanadium precursor and following thermal treatments. The FVO NPH photoelectrodes possess uniformly dispersed polyhedral nanocrystals that directly grow on the conductive substrate with tunable film thicknesses. The unique morphology enables an outstanding photo-electrocatalytic performance, and the optimized FVO NPH photoelectrode, which was annealed at 550 °C for 4 h with a film thickness of ∼560 nm, exhibits excellent photocurrent densities of ∼0.47 and ∼0.68 mA cm at 1.0 and 1.2 V vs. Ag/AgCl, respectively. After decorating CoPi co-catalyst, FVO/CoPi shows a highly efficient water splitting performance with O and H evolution rates of 7.53 and 15.32 μmol cm  h , respectively, which are ∼1.88 and ∼1.80 times, respectively, of these of the FVO NPH. The proposed photoelectrodes also show excellently chemical and physical stabilities in solar water splitting. This is the first time reported the preparation of well-organized nanostructured FeVO films, which warrants further optimization studies on morphologies and compositions of FeVO -based photoelectrodes.