Purpose: To investigate the influence of the etching strategy of universal adhesives on bond degradation to sound and artificially-induced caries-affected dentin.
Materials And Methods: The universal adhesives (Scotchbond Universal Adhesive; All-Bond Universal; Prime&Bond Elect) and adhesives used as controls (Adper Single Bond 2 and Clearfil SE Bond) were applied to sound and artificially-induced caries-affected bovine dentin. Microtensile bond strength was evaluated immediately (24 h) and after one year of water storage (1 year). Representative specimens were also prepared to assess nanoleakage. Bond strength data (MPa) were analyzed using three-way ANOVA and post-hoc Tukey's test (α = 0.05), considering each substrate separately.
Results: Bonding degradation was observed for all universal adhesives on caries-affected dentin, irrespective of the etching strategy. On sound dentin, bonding degradation was observed when adhesives were used on the etch-and-rinse strategy.
Conclusion: The universal adhesives were not capable of maintaining bond stability over time on caries-affected dentin. The self-etch strategy seems better able to maintain the durability of adhesive interfaces created on sound dentin.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.3290/j.jad.b1367889 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Cell-Based Glioma Models for Anticancer Drug Screening: From Conventional Adherent Cell Cultures to Tumor-Specific Three-Dimensional Constructs.
Cells
December 2024
School of Medicine and Life Sciences, Far Eastern Federal University, 690922 Vladivostok, Russia.
Gliomas are a group of primary brain tumors characterized by their aggressive nature and resistance to treatment. Infiltration of surrounding normal tissues limits surgical approaches, wide inter- and intratumor heterogeneity hinders the development of universal therapeutics, and the presence of the blood-brain barrier reduces the efficiency of their delivery. As a result, patients diagnosed with gliomas often face a poor prognosis and low survival rates.
View Article and Find Full Text PDFCoating Agents for Resin Composites: Effect on Color Stability, Roughness, and Surface Micromorphology Subjected to Brushing Wear.
Oper Dent
January 2025
*Roberta Tarkany Basting, DDS, MSc, PhD, Professor, Restorative Dentistry Department, Faculdade São Leopoldo Mandic, São Paulo, Brazil.
This study evaluated the influence of six resin composite coating agents on color stability and surface roughness after toothbrushing abrasion. Discs (Ø6 mm x 2 mm) of nanofilled resin composite (Filtek Z350XT) were prepared for application of coating agents (n=10): control (absence), two surface sealants (PermaSeal and BisCover LV), two adhesive systems (Scotchbond Multi-Purpose Adhesive/3M Oral Care and Single Bond Universal), and two modeling liquids (Modeling Resin and Composite Wetting Resin). CIELab*, WID, and color change (ΔEab, ΔE00, and ΔWID) were analyzed at baseline, after finishing and polishing, after application of coating agents, after coffee staining (simulating 30 days and one year of staining), and after toothbrushing abrasion.
View Article and Find Full Text PDFQuasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material.
J Vis Exp
December 2024
School of Engineering and Materials Science, Queen Mary University of London.
Article Synopsis
- The study evaluates the fracture strength of 1 mm-thick CAD/CAM occlusal veneers made from lithium disilicate (LD) and resin nanoceramics (RNC) to assess their viability in dental restoration.
- Using a novel testing protocol, the RNC group demonstrated a significantly higher load-bearing capacity compared to the LD group, indicating better durability under stress.
- Both materials experienced similar crack patterns during testing, emphasizing the importance of understanding mechanical properties for ensuring the longevity of dental restorations.
Bond strength comparison of chemically activated hard reline materials on CAD-CAM milled and conventional heat-polymerized PMMA denture bases.
J Prosthet Dent
January 2025
Assistant Professor, Department of Prosthodontic, College of Dental Medicine, Rangsit University, Phatum Thani, Thailand. Electronic address:
Statement Of Problem: Comprehensive data are needed on the performance of chemically activated, chairside hard reline materials when used with computer-aided design and computer-aided manufacturing (CAD-CAM) milled polymethyl methacrylate (PMMA) denture bases and conventionally processed bases. This lack of data affects decisions regarding the chairside reline material to be used for improving the fit and retention of relined complete dentures.
Purpose: The purpose of this in vitro study was to evaluate and compare the shear bond strength (SBS) of 3 chemically activated, chairside hard reline materials on CAD-CAM milled and conventional heat-polymerized PMMA denture bases.
The effect of different adhesive strategies and diamond burs on dentin bond strength of universal resin cements.
Clin Oral Investig
January 2025
Department of Restorative Dentistry, Graduate School of Dental Medicine, Hokkaido University, Sapporo, Japan.
Objectives: To evaluate the shear bond strength (SBS) of universal cements (UCs) to dentin prepared with different diamond burs using various adhesive strategies.
Materials And Methods: One-hundred-twenty molars were prepared to expose the mid-coronal dentin. The teeth were divided into two groups according to diamond bur preparations: coarse and super-fine grit burs.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!