Cortical Bone Modifications after Radiotherapy: Cortex Porosity and Osteonal Changes Evaluated Over Time.

Aiming to evaluate cortical bone microarchitecture and osteonal morphology after irradiation, twelve male New Zealand rabbits were used. The animals were divided: control group (no radiation-NIr); and 3 irradiated groups, sacrificed after: 7 (Ir7d); 14 (Ir14d) and 21 (Ir21d) days. A single radiation dose of 30 Gy was used. Computed microtomography analyzed the cortical microarchitecture: cortical thickness (CtTh), bone volume (BV), total porosity (Ct.Po), intracortical porosity (CtPo-cl), channel/pore number (Po.N), fractal dimension (FD) and degree of anisotropy (Ct.DA). After scan, osteonal morphology was histologically assessed by means: area and perimeter of the osteons (O.Ar; O.p) and of the Haversian canals (C.Ar; C.p). Microtomographic analysis were performed by ANOVA, followed by Tukey and Dunnet tests. Osteon morphology analyses were performed by Kruskal-Wallis, and test Dunn's. Cortical thickness was significant difference (p<0.010) between the NIr and irradiated groups, with thicker cortex at Ir7d (1.15±0.09). The intracortical porosity revealed significant difference (p<0.001) between irradiated groups and NIr, with lower value for Ir7d (0.29±0.09). Bone volume was lower in Ir14d compared to control. Area and perimeter of the osteons were statistically different (p<0.0001) between NIr and Ir7d. Haversian canals also revealed lower values (p<0.0001) in Ir7d (80.57±9.3; 31.63±6.5) compared to NIr and irradiated groups. Cortical microarchitecture was affected by radiation, and the effects appear to be time-dependent, mostly regarding the osteons morphology at the initial days. Cortex structure in Ir21d revealed similarities to control suggesting that microarchitecture resembles normal condition after a period.