Understanding the Hydrothermal Formation of NaNbO: Its Full Reaction Scheme and Kinetics.

Sodium niobate (NaNbO) attracts attention for its great potential in a variety of applications, for instance, due to its unique optical properties. Still, optimization of its synthetic procedures is hard due to the lack of understanding of the formation mechanism under hydrothermal conditions. Through X-ray diffraction, hydrothermal synthesis of NaNbO was observed in real time, enabling the investigation of the reaction kinetics and mechanisms with respect to temperature and NaOH concentration and the resulting effect on the product crystallite size and structure. Several intermediate phases were observed, and the relationship between them, depending on temperature, time, and NaOH concentration, was established. The reaction mechanism involved a gradual change of the local structure of the solid NbO precursor upon suspending it in NaOH solutions. Heating gave a full transformation of the precursor to HNaNbO·15HO, which destabilized before new polyoxoniobates appeared, whose structure depended on the NaOH concentration. Following these polyoxoniobates, NaNbO·HO formed, which dehydrated at temperatures ≥285 °C, before converting to the final phase, NaNbO. The total reaction rate increased with decreasing NaOH concentration and increasing temperature. Two distinctly different growth regimes for NaNbO were observed, depending on the observed phase evolution, for temperatures below and above ≈285 °C. Below this temperature, the growth of NaNbO was independent of the reaction temperature and the NaOH concentration, while for temperatures ≥285 °C, the temperature-dependent crystallite size showed the characteristics of a typical dissolution-precipitation mechanism.