Effect of deep rolling on subsurface conditions of CoCr28Mo6 wrought alloy to improve the wear resistance of endoprostheses.

Wear of orthopaedic endoprostheses is associated with adverse local and systemic reactions and can lead to early implant failure. Manufacturing determines the initial subsurface microstructure of an alloy that influences the implant's wear behaviour. Therefore, this study aims at generating enhanced wear resistances by a modification of the surface and subsurface microstructure of a CoCr28Mo6 wrought alloy by applying deep rolling. The state of the art was investigated by means of eleven retrieved CoCr28Mo6 hip implant components from different manufacturers with respect to their subsurface microstructure and micro hardness profiles. CoCr28Mo6 wrought alloy samples (DIN EN ISO 5832-12) were aged at 750 °C for 24 h and/or plastically deformed by deep rolling with varying axial forces (170 N, 230 N and 250 N). The samples were metallographically prepared and investigated using optical and scanning electron microscopy with EDS and EBSD, micro hardness testing, XRD and tribological testing. The retrieved implant components revealed that, independent of the manufacturer, neither the head nor the stem trunnion exhibited a defined subsurface condition. The dominant phase within the implants was face-centered cubic (fcc). Some implants exhibited single hexagonal close-packed (hcp) grains due to a stress-induced phase transformation. The initial CoCr28Mo6 wrought alloy had a fcc crystal structure. After isothermal aging, the matrix entirely transformed to a hcp structure. In the initial fcc-condition, deep rolling generated a plastically deformed surface layer within the first 100 μm and stress-induced phase transformation to hcp was observed. Micro hardness gradients were present in the subsurface of up to 600 μm depth and exhibited a maximum increase of 34% by deep rolling in comparison to the initial fcc-matrix. This trend was confirmed by a correlated increase in residual compressive stresses. In tribological tests under serum lubrication, the modified samples generated lower wear in comparison to the contemporarily used fcc-matrix samples. This study demonstrates that deep rolling is an effective processing to modify the subsurface of a biomedical CoCr28Mo6 wrought alloy in order to increase the wear resistance. The intentional transformation from the fcc to the hcp phase induced by deformation offers great potential for implant application.