The present study aimed to evaluate the bond strength of metal bracket (MB) and ceramic bracket (CB) bonded to different CAD/CAM ceramic substrates etched with hydrofluoric acid (HFA) vs. phosphoric acid (PA). A total of 120 CAD/CAM ceramic blocks in 12 groups were fabricated from three different CAD/CAM ceramic materials: VITABLOCS Mark II, VITAENAMIC, and IPS e.max CAD. Each ceramic material group was divided into two etching groups: one treated with 9.5% HFA and the other treated with 37%. Sixty metal and CBs of the upper right central incisor were bonded to the HFA-treated blocks. Another 60 metal and CBs were bonded to the PA treated blocks. All the bonded specimens were thermocycled before shear bond strength (SBS) testing. Then the bond failure mode was recorded There were no significant differences in SBS values between the three CAD/CAM ceramic materials. The HFA-treated specimens exhibited significantly higher SBS values than the PA-treated specimens. Also, the SBS values of CBs were significantly higher than the metal brackets (MBs). The adhesive remnant index (ARI) score was 4 for most of the groups, indicating that almost no adhesive remained on the porcelain surface. The CAD/CAM ceramic type did not influence SBS; however, HFA exhibited significantly higher SBS compared to PA.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC7867683 | PMC |
| http://dx.doi.org/10.34172/joddd.2020.042 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Determination of streptococcus mutans retention in acidic and neutral pH artificial saliva environment of all-ceramic materials with different surface treatment.
BMC Oral Health
January 2025
Department of Basic Medical Science, Faculty of Medicine, Yozgat Bozok University, Yozgat, 66100, Türkiye, Turkey.
Background: Although surface finishing processes are effective against Streptococcus mutans biofilm, the mechanism of action of saliva with different acidity values has not been studied in detail. This study aims to produce four different all-ceramic materials in a single session with CAD/CAM devices and apply two different surface finishing processes, glazing and polishing, and then determine the retention of Streptococcus mutants on the surfaces of the materials in saliva with varying levels of acidity.
Methods: Zirconia-reinforced lithium silicate (Vita Suprinity, Vita Zahnfabrik, Bad Saöckingen, Germany), monochromatic feldspar (Vitablocs Mark 2, Vita Zahnfabrik, Bad Saöckingen, Germany), leucite glass ceramic (IPS Empress CAD, Ivoclar Vivadent, Liechtenstein), and monolithic zirconia (Incoris TZI (Cerec) Sirona, Germany) were used in the study.
Translucency and contrast ratio of dimetharcyrlate resin based dental materials after bleaching: an in-vitro study.
BMC Oral Health
December 2024
Department of Restorative Dentistry, Faculty of Dentistry, Bolu Abant Izzet Baysal University, Bolu, Turkey.
Objective: To compare the translucency and contrast ratio of 13 different resin based restorative materials and to evaluate the effect of 2 different bleaching methods on the translucency and contrast ratio of these materials.
Methods: In this study, a total of 260 samples were prepared, 20 from each of 13 different dimethacrylate-based restorative materials. Then, each material group was divided into 4 subgroups.
Evaluation of Marginal Fit of CAD/CAM Ceramic Crowns and Scanning Time Using Different Intraoral Scanning Systems.
J Funct Biomater
November 2024
Department of Occlusion, Fixed Prosthodontics and Dental Materials, School of Dentistry, Federal University of Uberlandia, Uberlandia 38405-320, Minas Gerais, Brazil.
This study aimed to evaluate the scanning time and marginal fit of CAD/CAM crowns fabricated using different intraoral scanning systems (IOS) (O1-Omnicam 1.0, O2-Omnicam 2.0, PS-Primescan).
View Article and Find Full Text PDFFracture Resistance and Initial Penetration Time of a Novel Zirconia Crown Design for Simplifying Future Endodontic Treatment: An In Vitro Study.
Dent J (Basel)
November 2024
Department of Prosthetic Dental Science, College of Dentistry, Jazan University, Jazan 45142, Saudi Arabia.
: This study aimed to investigate the fracture strength of a novel-designed Zirconia crown before and after access opening, and to evaluate the mode of fracture and the time needed for initial penetration through the crown. : This study involved the design and testing of 60 zirconia crowns, divided into three groups (20 crowns each) to compare different structural designs. Group 1 (Control) used a conventional full zirconia crown.
View Article and Find Full Text PDFEvaluating fatigue resistance in occlusal veneers: a comparative study of processing techniques and material thickness of lithium disilicate (IPS e.max Press vs. IPS e.max CAD).
BMC Oral Health
December 2024
Department of Prosthodontics, Faculty of Dentistry, Chiang Mai University, Chiang Mai, Thailand.
Background: Lithium disilicate occlusal veneers are popular for minimally invasive posterior teeth restoration. The aim of this study was to compare the fatigue resistance and crack pattern of lithium disilicate occlusal veneers fabricated using pressing and milling techniques with varying thicknesses.
Methods: Sixty lithium disilicate discs, representing occlusal veneers, were divided into four groups (n = 15) based on processing technique (IPS e.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!