The paper presents the influence of laboratory aging simulation on fracture properties determined on 150 variants of asphalt mixtures. The fracture properties were determined by two different test approaches-semi-circular bending test (SCB test) and three-point bending test on beam specimens (3-PB test). The aging was simulated according to one of the methods defined in EN 12697-52 (storage of test specimens in chamber at temperature of 85 °C for 5 days). The evaluated group of variants covered asphalt mixtures for all road layers. The group was further divided according to used bituminous binder (unmodified vs. modified) and reclaimed asphalt content. The results showed that strength parameters (flexural strength and fracture toughness) increase with aging. It further shows that fracture work provides more complex information about the cracking behavior. For the aging indexes, it was found that for mixtures with modified binders and mixtures which did not contain reclaimed asphalt (RA), the values were higher. The aging indexes for fracture work showed different results for both performed tests.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC7915930 | PMC |
| http://dx.doi.org/10.3390/ma14040811 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Simplified Model for the Behaviour of Asphalt Mixtures Depending on the Time and the Frequency Domain.
Materials (Basel)
January 2025
Department of Highway and Railway Engineering, Budapest University of Technology and Economics, Műegyetem Rakpart 3, H-1111 Budapest, Hungary.
Sigmoid functions are widely used for the description of viscoelastic material properties of asphalt mixtures. Unfortunately, there are still no known closed functions for describing connections among model parameters in the time and the frequency domains. In most cases, complicated interconversion methods are applied for the conversion of viscoelastic material properties.
View Article and Find Full Text PDFNumerical testing method and mechanical property evaluation of large particle size asphalt mixture.
PLoS One
January 2025
Key Laboratory for Special Area Highway Engineering of Ministry of Education, Chang'an University, Xi'an, Shaanxi, China.
The large particle size asphalt mixture with nominal maximum aggregate size 53 mm(LSAM-50) has good technical and economic performance and will become an effective technical way to build a full-thick long-life asphalt pavement with Chinese characteristics. In order to reveal the mechanical properties and influencing factors of LSAM-50 in depth, a numerical test method for the mechanical properties of the large particle size LSAM-50 asphalt mixture was developed, and a reasonable specimen size for LSAM-50 performance test was proposed by combining the numerical test and the indoor test. The results show that: LSAM-50 numerical test conditions are the calculation time step 10-3 s/step, the loading rate is 2 mm/min (uniaxial compression numerical test) and 50 mm/min (splitting numerical test) when LSAM-50 numerical experiment calculation rate and numerical experiment accuracy are better; after the size of the specimen reaches 200×160mm, the influence of the size effect is eliminated.
View Article and Find Full Text PDFStudy on Water Damage of Asphalt-Aggregate Based on Molecular Dynamics.
Materials (Basel)
January 2025
College of Civil Engineering and Architecture, Shandong University of Science and Technology, Qingdao 266590, China.
To investigate the water damage at the interface between emulsified asphalt and aggregate under the action of external water infiltration, firstly, cetyltrimethylammonium bromide was used as an emulsifier to prepare emulsified asphalt in the laboratory, and its basic properties were tested. Then, based on molecular dynamics, an emulsified asphalt-aggregate interface model with different water contents was constructed to calculate the adhesion work of the emulsified asphalt-aggregate interface. The results show that the simulated values of emulsified asphalt density, cohesive energy density, and solubility are in good agreement with the experimental values.
View Article and Find Full Text PDFInvestigation of Chloride Salt Erosion on Asphalt Binders and Mixtures: Performance Evaluation and Correlation Analysis.
Materials (Basel)
January 2025
College of Engineering, Zhejiang Normal University, Jinhua 321004, China.
Asphalt pavement, widely utilized in transportation infrastructure due to its favourable properties, faces significant degradation from chloride salt erosion in coastal areas and winter deicing regions. In this study, two commonly used asphalt binders, 70# base asphalt and SBS (Styrene-Butadiene-Styrene)-modified asphalt, were utilized to study the chloride salt erosion effect on asphalt pavement by immersing materials in laboratory-prepared chloride salt solutions. The conventional properties and adhesion of asphalt were assessed using penetration, softening point, ductility, and pull-off tests, while Fourier transform infrared spectroscopy (FTIR) elucidated the erosion mechanism.
View Article and Find Full Text PDFEffects of Moisture Infiltration on Interfacial Characteristics of Fiber Asphalt Mastic-Aggregate and the Cracking Resistance of Mixture.
Materials (Basel)
December 2024
College of Civil Science and Engineering, Yangzhou University, Yangzhou 225100, China.
Article Synopsis
- The study examines how moisture affects the bond between fiber asphalt mixtures and aggregate, impacting their cracking resistance.
- Researchers tested three types of fiber (basalt, glass, polyester) at various contents and used specific tests to measure interfacial strength.
- Results indicated that while fibers improve interfacial strength, moisture infiltration significantly weakens it, influencing the overall durability of asphalt pavement.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!