Dynamic measurement of amnion thickness during loading by speckle pattern interferometry.

Introduction: In previous studies on the mechanical parameters of amnions (AM), there is a limitation due to the lack of an accurate thickness measurement, which is an important parameter for determining AM-specific mechanical properties. As a bottleneck, the characterization of the basic mechanical properties of AM are greatly restricted, even with the proposal of fracture criteria.

Method: First, the initial thickness of the AM is estimated by the interpolated-volume-area method. Second, through combinations of our self-developed mini-biaxial tensile device with speckle pattern interferometry, this is the first time that researchers can accurately obtain the AM thickness at each transient moment in the process of loading.

Results: Based on the experimental results, an accurate stress-strain curve could be obtained. Two important mechanical parameters-the fracture energy density and amnion rupture modulus-could be extracted as 0.184±0.036MPa and 108.57±17.32MPa, respectively. The fracture energy density and amnion rupture modulus provide objective criteria and a scientific basis for the evaluation of AM rupture.

Discussion: The tensile stress-strain curve of a normal human amnion shows a distinct J-shape. This proves that the experimental results are basically reliable. Both important parameters --the fracture energy density and amnion rupture modulus, can be calculated from the stress-strain curve. Extracting these two parameters is critical for the evaluation and prediction of ROM, PROM and PPROM.