The formation of molybdenum diselenide (MoSe2) is widely observed at the back-contact interface for copper zinc tin selenide (CZTSe) thin-film solar cells. Depending on individual selenium (Se) supply and thermal conditions for forming CZTSe absorbers on molybdenum (Mo) substrates, the thickness of MoSe2 can vary from a few hundreds of nanometers up to ≈ 1 μm, which is comparable to the commonly adopted thickness of 1 ~ 1.5 μm for CZTSe absorbers. In this study, for controlling the thickness of interfacial MoSe2, thin diffusion barrier layers of silicon oxynitride (SiOxNy) are deposited onto Mo layers prior to the growth of CZTSe absorbers in the fabrication process. As a result, a reduction in the thicknesses of MoSe2 layers is achieved. In terms of energy conversion efficiency (η), CZTSe solar cells grown on Mo/SiOxNy back contacts suffer a deterioration as the SiOxNy layers get thicker. CZTSe solar cells grown on Mo/SiOxNy/Mo back contacts preserve their efficiencies at ≈ 11% with thin 10 nm SiOxNy layers.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC7802926 | PMC |
| http://journals.plos.org/plosone/article?id=10.1371/journal.pone.0245390 | PLOS |
Publication Analysis
Top Keywords
Similar Publications
Nanoscale Effects in the Room-Temperature UV-Visible Photoluminescence from Silica Particles and Its Cancer Cell Imaging.
Bioconjug Chem
January 2025
Department of Physics, Indian Institute of Technology Roorkee, Roorkee 247667, Uttarakhand, India.
Silica nano/microparticles have generated significant interest for the past decades, emerging as a versatile material with a wide range of applications in photonic crystals, bioimaging, chemical sensors, and catalysis. This study focused on synthesizing silica nano/microparticles ranging from 20 nm to 1.2 μm using the Stöber and modified Stöber methods.
View Article and Find Full Text PDFRhodanine Substitution of Asymmetric Nonfullerene Acceptors for High-Performance Organic Solar Cells.
ACS Appl Mater Interfaces
January 2025
College of Biological, Chemical Sciences and Engineering, Jiaxing University, Jiaxing, Zhejiang 314001, China.
Asymmetric substitution is acknowledged as a straightforward yet potent approach for the optimization of small molecule acceptors (SMAs), thereby enhancing the power conversion efficiency (PCE) of organic solar cells (OSCs). In this work, we have successfully engineered and synthesized a novel asymmetric SMA, designated as Y6-R, which features a rhodanine-terminated inner side-chain. In devices with PM6 as the polymer donor, the asymmetric Y6-R demonstrated an impressive PCE of 18.
View Article and Find Full Text PDFSN2-Reaction-Driven Bonding-Heterointerface Strengthens Buried Adhesion and Orientation for Advanced Perovskite Solar Cells.
Angew Chem Int Ed Engl
January 2025
Shandong University of Science and Technology, Institute of Carbon Neutrality, College of Chemical and Biological Engineering, No 579 Qianwangang Road, Huangdao District, 266590, Qingdao, CHINA.
Traditionally weak buried interaction without customized chemical bonding always goes against the formation of high-quality perovskite film that highly determines the efficiency and stability of perovskite solar cells. To address this issue, herein, we propose a bimolecular nucleophilic substitution reaction (SN2) driving strategy to idealize the robust buried interface by simultaneously decorating underlying substrate and functionalizing [PbX6]4- octahedral framework with iodoacetamide and thiol molecules, respectively. Theoretical and experimental results demonstrate that a strong SN2 reaction between exposed halogen and thiol group in two molecules occurs, which not only benefits the reinforcement of buried adhesion, but also triggers target-point-oriented crystallization, synergistically upgrading the upper perovskite film quality and accelerating interfacial charge extraction-transfer behavior.
View Article and Find Full Text PDFIn-situ Polymerization Induced Seed-Root Anchoring Structure for Enhancing Stability and Efficiency in Perovskite Solar Modules.
Angew Chem Int Ed Engl
January 2025
Southern University of Science and Technology, Department of Mechanical and Energy Engineering, 1088 Xueyuan Blvd, Nanshan District, 518055, Shenzhen, CHINA.
The escape of organic cations over time from defective perovskite interface leads to non-stoichiometric terminals, significantly affecting the stability of perovskite solar cells (PSCs). How to stabilize the interface composition under environmental stress remains a grand challenge. To address this issue, we utilize thiol-functionalized particles as a "seed" and conduct in situ polymerization of 2,2,3,4,4,4-hexafluorobutyl methacrylate (HFMA) as a "root" at the bottom of the perovskite layer.
View Article and Find Full Text PDFAdvanced room-temperature cured encapsulant film for crystalline silicon solar modules: enhancing efficiency with luminescent down-shifting, flame retardancy, and UV resistance.
Mater Horiz
January 2025
State Key Laboratory of Organic-Inorganic Composites, College of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China.
Solar energy sources have garnered significant attention as a renewable energy option. Despite this, the practical power conversion efficiency (PCE) of widely used silicon-based solar cells remains low due to inefficient light utilization. In this study, carbon dots (APCDs) were prepared a hydrothermal method using ammonium polyphosphate and -phenylenediamine, then incorporated into a silicone-acrylic emulsion (CAS) to create a luminescent down-shifting (LDS) layer for solar cells.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!