Biomolding Technique to Fabricate the Hierarchical Topographical Scaffold of POMA To Enhance the Differentiation of Neural Stem Cells.

In this paper, a biomolding technique was first used to fabricate a scaffold of hierarchical topography with biomimetic morphology for tissue engineering. First, poly(-methoxyaniline) (POMA) was synthesized by conventional oxidative polymerization, followed by characterizations with Fourier transform infrared spectroscopy (FTIR) and gel permeation chromatography (GPC). Moreover, the POMA scaffold with 3D biomimetic morphology was fabricated using poly(dimethylsiloxane) (PDMS) as negative soft template from natural leaf surfaces of , followed by transferring the pattern of PDMS template to POMA. The as-fabricated POMA scaffold with biomimetic morphology was investigated by scanning electron microscopy (SEM). Subsequently, cell-scaffold interactions were carried out by culturing rat neural stem cells (rNSCs) on biomimetic and nonbiomimetic, or flat, POMA scaffolds, as well as on poly(d-lysine) (PDL)-coated substrate, and evaluating the corresponding adhesion, cell viability, and differentiation of rNSCs. Results showed that there was no significant difference in the attachment of rNSCs on the three surface types, however, both the biomimetic and flat POMA scaffolds induced growth arrest relative to the PDL-coated substrate. In addition, the percentage of cells with elongated neurites after 19 days of culture was higher on the biomimetic POMA scaffold relative to flat POMA and PDL. In summary, the POMA scaffold with biomimetic morphology shows promise in promoting rNSCs differentiation and neurite outgrowth for long-term studies on nerve regenerative medicine.