Influence of Oxidation Damages on Mechanical Properties of SiC/SiC Composite Using Domestic Hi-Nicalon Type SiC Fibers.

Here, we show that when the oxidation treatment temperature exceeded 600°C, the tensile strength of SiC/SiC begins to decrease. Oxidation leads to the damages on the PyC fiber/matrix interface, which is replaced by SiO at higher temperature. The fracture mode converts from fiber pull-out to fiber-break as the fiber/matrix interface is filled with SiO. Oxidation time also plays an important role in affecting the tensile strength of SiC/SiC. The tensile modulus decreases with temperature from RT to 800°C, then increases above 800°C due to the decomposition of remaining CSi O and crystallization of the SiC matrix. A special surface densification treatment performed in this study is confirmed to be an effective approach to reduce the oxidation damages and improve the tensile strength of SiC/SiC after oxidation.