Effect of different surface treatments on shear bond strength of ceramic brackets to old composite.

Background: At present, the demand for orthodontic treatment is on the rise. On the other hand, evidence shows that the bond strength of composite resins to old composite restorations is often unreliable. Therefore, the aim of this in vitro study was to assess the effect of different surface treatments on shear bond strength (SBS) of ceramic brackets to old composite restorations.

Methods: In this in vitro experimental study, 60 nano-hybrid composite discs were fabricated. For aging, the discs were incubated in deionized water at 37 °C for 1 month. Next, they underwent 4 different surface treatments namely acid etching with 37% phosphoric acid, sandblasting, grinding, and Er,Cr:YSGG laser irradiation. Ceramic brackets were then bonded to the discs and underwent SBS testing.

Results: The maximum mean SBS value was obtained in the grinding group (9.16 ± 2.49 MPa), followed by the sandblasting (8.13 ± 2.58 MPa) and laser (6.57 ± 1.45 MPa) groups. The minimum mean SBS value was noted in the control group (5.07 ± 2.14 MPa).

Conclusion: All groups except for the control group showed clinically acceptable SBS. Therefore, grinding, sandblasting, and Er,Cr:YSGG laser are suggested as effective surface treatments for bonding of ceramic orthodontic brackets to aged composite.