Objectives: Testing and comparing of different non-shaded zirconia materials (3Y-TZP, 4Y-TZP and 5Y-TZP) on optical and mechanical properties.
Materials And Methods: Zirconia materials (N = 320, Opaque O, Translucent T, Extra Translucent ET, High Translucent HT) were investigated on translucency, Martens parameter, biaxial flexural strength, Chevron-Notch-Beam (CNB) fracture toughness (K) and grain size. The grain size was analyzed using a scanning electron microcopy (SEM). Univariate ANOVA, post-hoc Scheffé, partial eta-squared, Kolmogorov-Smirnov-, Kruskal-Wallis- and Mann-Whitney-U-tests (p < 0.05) were performed. The reliability of flexural strength was calculated with two-parametric Weibull analysis and 95 % confidence level.
Results: The translucency of ET and HT increased with the thermo-mechanical aging (p < 0.001). The zirconia material and aging had no impact on the Martens hardness and the indentation modulus. ET showed the highest flexural strength values after initial and thermo-mechanical aging (p < 0.001 - 0.683). All four materials showed the highest flexural strength after thermo-mechanical aging after 1.2 Mio cycles. Thermo-mechanically (1.2 Mio cycles) aged HT presented the highest Weibull modulus (m = 15.0) regardless of aging. Within initial groups, T (p ≤ 0.001) showed the highest fracture toughness, followed by O (p ≤ 0.001), ET (p < 0.003) and HT (p ≤ 0.001).
Significance: Translucency of ET and HT increases with thermo-mechanical aging. Chevron-Notch-Beam (CNB) is a valid alternative to the single-edge-V-notched beam (SEVNB) method for testing fracture toughness.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.dental.2020.11.007 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
The Impact of an MDP-Containing Primer on the Properties of Zinc Oxide Networks Infiltrated with BisGMA-TEGDMA and UDMA-TEGDMA Polymers.
Materials (Basel)
December 2024
Department of Prosthodontics, Propaedeutics and Dental Materials, School of Dentistry, Christian-Albrechts University at Kiel, Arnold-Heller-Straße 16, 24105 Kiel, Germany.
This study was conducted to evaluate the material properties of polymer-infiltrated zinc oxide networks (PICN) and the effect of using a phosphate monomer-containing primer applied before polymer infiltration. A total of 148 ZnO-network (zinc oxide) specimens were produced: = 74 were treated with a primer before polymer infiltration and light curing, while the remaining specimens were untreated. Each group was divided into two subgroups ( = 37) based on the infiltrating polymer: UDMA (aliphatic urethane-dimethacrylates)-TEGDMA (triethylene glycol-dimethacrylate) or BisGMA (bisphenol A-glycidyl-methacrylate)-TEGDMA.
View Article and Find Full Text PDFEffects of home bleaching agents on hybrid ceramics: mechanical properties and color change.
BMC Oral Health
January 2025
Department of Fixed Prosthodontics - Faculty of Dentistry, Ain Shams University, Organization of African Unity, St, El-Qobba Bridge, El Weili, Cairo Governorate, Egypt.
Background: Home bleaching is a promising option for addressing discolored teeth conservatively. However, its impact on the physical and mechanical properties of indirect restorations remains unknown. This study provides comparative insights into the material responses to aesthetic treatments by assessing the effects of home bleaching agents on two hybrid ceramics: VITA ENAMIC and Grandio Blocs.
View Article and Find Full Text PDFEffect of extrinsic pigmentation and multiple firing cycles on the properties of a zirconia-containing lithium silicate ceramic.
J Prosthodont
January 2025
Department of Dentistry, Federal University of Rio Grande do Norte (UFRN), Lagoa Nova, Natal, Brazil.
Purpose: To assess the impact of staining and multiple firings on the mechanical, optical, and surface characteristics of zirconia-containing lithium silicate ceramics (ZLS).
Materials And Methods: Ninety ZLS discs (Suprinity, VITA Zahnfabrick) were divided according to the "Number of firings" protocol: Ctr-control, no characterization; SC-single firing cycle (for characterization, crystallization and staining simultaneously); and DC-double firing cycle (crystallization firing cycle was performed separately from the staining firing). Extrinsic pigmentation was performed to replicate the characterization of a monolithic restoration.
Crystallization by microwave energy: Effects on the survival probability of lithia-based glass ceramics.
Braz Oral Res
January 2025
Universidade Estadual Paulista - Unesp, Institute of Science and Technology, Department of Dental Materials and Prosthodontics, São José dos Campos, SP, Brazil.
This study evaluated the survival probabilities of two lithia-based glass-ceramics after final crystallization in a microwave furnace using conventional crystallization as a reference. Disc-shaped samples of a lithium silicate (LS, Celtra Duo) and a lithium disilicate (LD, e.max CAD) were prepared and divided into two groups according to the crystallization method (n = 30): microwave (M) or conventional furnaces (C).
View Article and Find Full Text PDFDentin remineralization induced by experimental composites containing calcium orthophosphate particles.
Dent Mater
December 2024
University of São Paulo School of Dentistry, Department of Biomaterials and Oral Biology, Av. Prof. Lineu Prestes, 2227, São Paulo, SP 05508-000, Brazil. Electronic address:
Objectives: This study aimed to verify if composites containing dicalcium phosphate dihydrate particles (DCPD) are able to induce dentin remineralization in vitro. Additionally, the mechanical properties of the materials were tested.
Methods: Four composites with 50 vol% inorganic content and 1 BisGMA: 1 TEGDMA (mols) were prepared, with different DCPD:glass ratios (50:0, 40:10, 30:20 and 0:50).
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!