An comparative evaluation of the effect of three endodontic chelating agents (17% ethylenediamine tetraacetic acid, 1% peracetic acid, 0.2% chitosan) on the push out bond strength of gutta percha with a new bioceramic sealer (BioRoot RCS).

Aim: This study aims to evaluate the effect of three endodontic chelating agents (17% ethylenediamine tetra-acetic acid [EDTA], 1% peracetic acid [PAA], 0.2% Chitosan) on the push out bond strength of gutta percha with a new bioceramic sealer (BioRoot RCS).

Materials And Methods: Forty-eight single-rooted mandibular premolars were selected and decoronated to obtain standardized root length of 15 mm. The root canals were prepared up to #30 files (Hyflex CM) and copious irrigation was done with 3 ml of 5.25% of NaOCl. According to the final irrigation, specimens were divided into three groups: Group 1 ( = 16) 0.2% chitosan, Group 2 ( = 16) 17% EDTA, and Group 3 ( = 16) 1% PAA for 1 min. Samples from each group were obturated with bioceramic sealer and gutta percha and sealed with temporary filling material. Two horizontal slices of 2 mm was obtained from the middle third of each sample ( = 32). Push out bond strength and failure modes were assessed. Kruskal-Wallis test followed by Mann-Whitney analysis was used for push out analysis. Chi square test was used to compare the modes of failure. The statistical significance level was set at = 0.05.

Results: The highest push out bond strength was obtained with Group 1 (0.2% chitosan) followed by Group 3 (1% PAA). Group 2 (17% EDTA) showed least push out bond strength when compared to Group 1 (0.2% chitosan) and Group 3 (1% PAA). The mode of failure was mainly cohesive for all groups.

Conclusions: The highest push-out bond strength of BioRoot RCS was seen after treatment with 0.2% chitosan while the least was after EDTA treatment. 1% PAA treatment also favorably affected push-out bond strength of BioRoot RCS.