This study aims to evaluate the impact of adding a novel tricyclodecane dimethanol diacrylate comonomer on the flexural strength (FS) and impact strength (IS) of heat-cure denture base resin at 10% and 20% (v/v) concentrations. To test the FS and IS, a sum total of 150 bar-shaped specimens were prepared according to standard specifications. For the FS, the specimens were subjected to the three-point bend test with a span length of 50 mm. For the IS, Charpy's test was executed with a span length of 60 mm. The FS was measured in MPa, and the IS was measured in kJ/m. There was a statistically significant difference (P < 0.001) between the control and experimental groups in that both the FS and IS were increased in the experimental groups relative to the control group.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.2334/josnusd.19-0493 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
The Influence of the Comonomer Ratio and Reaction Temperature on the Mechanical, Thermal, and Morphological Properties of Lignin Oil-Sulfur Composites.
Molecules
September 2024
Department of Chemistry and Center for Optical Materials Science and Engineering Technology, Clemson University, Clemson, SC 29634, USA.
Although lignin is a plentiful biomass resource, it continually exists as an underutilized component of biomass material. Elemental sulfur is another abundant yet underutilized commodity produced as a by-product resulting from the refining of fossil fuels. The current study presents a strategy for preparing five durable composites via a simple one-pot synthesis involving the reaction of lignin oil and elemental sulfur.
View Article and Find Full Text PDFSynthesis of polymerizable betulin maleic diester derivative for dental restorative resins with antibacterial activity.
Dent Mater
June 2024
State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Materials Science and Engineering, Donghua University, Shanghai 201620, China.
Objective: Bisphenol A glycidyl methacrylate (Bis-GMA) is of great importance for dental materials as the preferred monomer. However, the presence of bisphenol-A (BPA) core in Bis-GMA structure causes potential concerns since it is associated with endocrine diseases, developmental abnormalities, and cancer lesions. Therefore, it is desirable to develop an alternative replacement for Bis-GMA and explore the intrinsic relationship between monomer structure and resin properties.
View Article and Find Full Text PDFChemical Modification of Dental Dimethacrylate Copolymer with Tetramethylxylylene Diisocyanate-Based Quaternary Ammonium Urethane-Dimethacrylates-Physicochemical, Mechanical, and Antibacterial Properties.
Materials (Basel)
January 2024
Department of Physical Chemistry and Technology of Polymers, Faculty of Chemistry, Silesian University of Technology, Strzody 9 Str., 44-100 Gliwice, Poland.
In this study, two novel quaternary ammonium urethane-dimethacrylates (QAUDMAs) were designed for potential use as comonomers in antibacterial dental composite restorative materials. QAUDMAs were synthesized via the reaction of 1,3-bis(1-isocyanato-1-methylethyl)benzene with 2-(methacryloyloxy)ethyl-2-decylhydroxyethylmethylammonium bromide (QA10+TMXDI) and 2-(methacryloyloxy)ethyl-2-dodecylhydroxyethylmethylammonium bromide (QA12+TMXDI). Their compositions with common dental dimethacrylates comprising QAUDMA 20 wt.
View Article and Find Full Text PDFMulticomponent Acrylic Formulation Design for Corrosion Casting with Controlled Mechanical Properties.
Polymers (Basel)
July 2023
Laboratory of Veterinary Morphology, Faculty of Veterinary Sciences, Ghent University, Salisburylaan 133, 9820 Merelbeke, Belgium.
Corrosion casting based on the curing of acrylic resins enables one to create casts as replicas of body systems, enhancing our knowledge of veterinary medicine. The identification of the optimal chemical formulations as well as the processing conditions, the delivery of good control during the liquid state and the excellent macroscopic properties during solidification and after use are remaining challenges. In the present work, based on the identification of more qualitative trends, it is demonstrated that multicomponent comonomer mixtures are interesting materials that can be used to expand the range of mechanical properties and can specifically result in a better balance between stiffness and flexibility while guaranteeing dimensional stability.
View Article and Find Full Text PDFThermomechanical Properties and Fracture Toughness Improvement of Thermosetting Vinyl Ester Using Liquid Metal and Graphene Nanoplatelets.
Polymers (Basel)
December 2022
School of Engineering, Swinburne University of Technology, P.O. Box 218, Melbourne, VIC 3122, Australia.
In this study, a eutectic gallium-indium (EGaIn) alloy and graphene nanoplatelets (GnPs) were employed as reinforcements for a comonomer vinyl ester (cVE) resin at different weight fractions up to 2% via a direct polymerization process. First, the effect of EGaIn on the curing kinetics of cVE was evaluated. The thermal and mechanical properties, and the fracture toughness of two types of cVE composites consisting of EGaIn and GnPs were then studied.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!