Objective: The effect of cusp angle on the load-carrying capacity and failure behaviour of BionZ Diamond zirconia crowns is carried out using experimental and numerical investigations.
Methods: The experimental program using monolithic crowns were divided into three groups (n = 14) for three cusp angles, 60, 80 and 120 degrees and were tested to failure under the static load. A 2-channel acoustic emission (AE) system was used to monitor the failure process while the piezo sensors were attached to the rigid stainless-steel jig for recoding the AE events. Load-displacement and AE response were simultaneously monitored until failure of specimens. Parametric AE analysis was conducted for the factors such as amplitude, energy released, signal duration and cumulative counts, for each AE signal. Fast Fourier transform (FFT) was conducted to assess the frequency at failure. Linear finite element analysis (FEA) was carried out using commercial software Ansys Workbench 19.1 to present the stress distribution and failure modes. Post-failure surface morphology study was carried out using scanning electron microscopy (SEM) and statistical analysis was performed using Weibull analysis.
Results: All the samples in three different groups have failed at the mid-line, splitting the zirconia crowns into two equal pieces. The load to failure was directly proportional to the cusp angle in crowns; 120° group had the highest load-carrying capacity of 2.93 ± 0.26 kN while 60 and 80° groups had a failure load of 2.46 ± 0.53 and 2.52 ± 0.16 kN, respectively. Parametric AE analysis revealed that the failure was instantaneous and 60-degree samples had higher AE signature. FE analysis showed the crack initiation at the occlusal surface of the crown which is in agreement with the SEM images. A close agreement of results for the load and stress distribution from FEA complemented with the experimental study.
Significance: Optimisation of cusp-angle could help clinicians to accurately design the monolithic zirconia crown focussing on maximum load-carrying capacity, increasing the restoration life.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.dental.2020.09.007 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Wave-absorbing honeycombs have garnered widespread attention due to their high-efficiency absorption, ultra-wideband absorption, lightweight nature, and high load-carrying capacity. However, as electromagnetic radiation power increases, the temperature of the absorbing honeycomb increases rapidly, even leading to burning. Therefore, it is significant to possess an efficient and accurate assessment of the thermal effects of absorbing honeycombs under electromagnetic radiation.
View Article and Find Full Text PDFHybrid molecular-scale and continuum modeling of two-dimensional flow between inhomogeneous solid surfaces and its application to the thrust bearing.
J Mol Model
January 2025
College of Mechanical Engineering, Changzhou University, Changzhou, Jiangsu Province, China.
Context: The flow equations are derived for describing the two-dimensional hybrid molecular-scale and continuum flows in the very small surface separation with inhomogeneous solid surfaces and they can be applied for designing the specific bearings. The aim of the present study is to solve this specific flow problem in engineering with normal computational cost. The flow factor approach model describes the flow of the molecule layer adjacent to the solid surface and the Newtonian fluid model describes the flow of the intermediate continuum fluid.
View Article and Find Full Text PDFMultiscale Numerical Study of Enhanced Ductility Ratios and Capacity in Carbon Fiber-Reinforced Polymer Concrete Beams for Safety Design.
Polymers (Basel)
January 2025
Department of Civil and Environmental Engineering, Ben-Gurion University of the Negev, Beer Sheva 8410501, Israel.
Rigid reinforced concrete (RC) frames are generally adopted as stiff elements to make the building structures resistant to seismic forces. However, a method has yet to be fully sought to provide earthquake resistance through optimizing beam and column performance in a rigid frame. Due to its high corrosion resistance, the integration of CFRP offers an opportunity to reduce frequent repairs and increase durability.
View Article and Find Full Text PDFFlexural Response Comparison of Nylon-Based 3D-Printed Glass Fiber Composites and Epoxy-Based Conventional Glass Fiber Composites in Cementitious and Polymer Concretes.
Polymers (Basel)
January 2025
School of Civil Engineering and Environmental Science, University of Oklahoma, 202 W Boyd St., Norman, OK 73019, USA.
With 3D printing technology, fiber-reinforced polymer composites can be printed with radical shapes and properties, resulting in varied mechanical performances. Their high strength, light weight, and corrosion resistance are already advantages that make them viable for physical civil infrastructure. It is important to understand these composites' behavior when used in concrete, as their association can impact debonding failures and overall structural performance.
View Article and Find Full Text PDFExpansion Characteristics and Shear Behavior of Reinforced Concrete Beams Under Non-Uniform Expansion Induced by Alkali-Silica Reaction.
Materials (Basel)
January 2025
Engineering Research Centre of Diagnosis Technology of Hydro-Construction, Chongqing Jiaotong University, Chongqing 400074, China.
Alkali-silica reaction (ASR) is an important factor that seriously affects the durability of reinforced concrete (RC) structures. The current research on alkali-aggregate mainly focuses on the deterioration mechanism of materials and the mechanical properties of standard specimens. However, there is a gap in the field of research on the effect of alkali-aggregate damage on the level of RC structures.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!