Synthesis of an Al-Based Composite Reinforced by Multi-Phase ZrB, AlBC and AlO with Good Mechanical and Thermal Properties at Elevated Temperature.

To synthesize Al composite with high strength at elevated temperature, high modulus and thermal stability, ZrB, AlBC and AlO particles have been chosen as reinforcements simultaneously. A (9.2 wt.% ZrB + 5.6 wt.% AlBC + 5.5 wt.% AlO)/Al composite has been prepared, and the in-situ synthesized particles are nano-sized. Mechanical property tests reveal that the nanoparticles exhibit a remarkable synergistic enhancement effect. The elasticity modulus of the composite is 89 GPa, and the ultimate tensile strengths at 25 °C and 350 °C can be as high as 371 MPa and 154 MPa, respectively.