Transport and Point Contact Measurements on PrCePtGe Superconducting Polycrystals.

We performed a detailed investigation of the superconducting properties of polycrystalline PrCePtGe pellets. We report the effect of Ce substitution, for x = 0.07, on magnetic field phase diagram H-T. We demonstrate that the upper critical field is well described by the Ginzburg-Landau model and that the irreversibility field line has a scaling behaviour similar to cuprates. We also show that for magnetic fields lower than 0.4 T, the activation energy follows a power law of the type ?, suggesting a collective pinning regime with a quasi-2D character for the Ce-doped compound with x = 0.07. Furthermore, by means of a point contact Andreev reflection spectroscopy setup, we formed metal/superconductor nano-junctions as small as tens of nanometers on the PrPtGe parent compound (x = 0). Experimental results showed a wide variety of conductance features appearing in the dI/dV vs. V spectra, all explained in terms of a modified Blonder-Tinkham-Klapwijk model considering a superconducting order parameter with nodal directions as well as sign change in the momentum space for the sample with x = 0. The numerical simulations of the conductance spectra also demonstrate that s-wave pairing and anisotropic s-waves are unsuitable for reproducing experimental data obtained at low temperature on the un-doped compound. Interestingly, we show that the polycrystalline nature of the superconducting PrPtGe sample can favour the formation of an inter-grain Josephson junction in series with the point contact junction in this kind of experiments.