Antimony has been listed as a critical pollutant in many countries because of its toxic effects on earth organisms. In this study, titanate nanosheets (TNS) were prepared with a high specific surface area by alkaline hydrothermal method. The adsorption mechanism and adsorption capacity of removing Sb(III) from aqueous solutions with TNS as an adsorbent were investigated for the first time. The FTIR and XPS analysis indicated that the interlayer sodium ions of TNS were responsible for Sb(III) adsorption. The batch experiments were conducted on solution pH, adsorbent dosage, initial concentration and reaction time. The results exhibited that when pH was 2, the removal rate was about 90% with the dosage of TNS was 0.1 g/L. The adsorption reaction was exceedingly rapid in the initial 5 min, and then the reaction was in equilibrium after about 30 min. The experimental data were better fitted with Langmuir isotherm model, and the maximum adsorption amount could attain 232.56 mg/g. The experiments showed that TNS had outstanding anti-interference performance to common cations. Therefore, TNS were considered to be an excellent material for removing Sb(III) from aqueous solutions.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.1016/j.ecoenv.2020.111271 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Visual Location of Oxygen Vacancies on Bismuth Titanate Nanosheets with Periodic Quantum Well and Promoting HO Photosynthesis.
Small
January 2025
Shandong Provincial Key Laboratory of Molecular Engineering, School of Chemistry and Chemical Engineering, Qilu University of Technology (Shandong Academy of Sciences), Jinan, Shandong, 250353, P. R. China.
Oxygen vacancy (OV) defect engineering plays a crucial role in enhancing photocatalytic efficiency. However, the direct visual characterization of oxygen vacancies still remains technically limited. Herein, a bismuth titanate (BiTiO, BTO-OV) model photocatalyst containing oxygen vacancies is constructed through density functional theory (DFT) calculations to reveal the influence mechanism of distinctive periodic quantum well and oxygen vacancies on the charge transfer behavior in BTO.
View Article and Find Full Text PDFStrategically Designed Ternary Nanohybrids of Titanate Nanosheet and Polydopamine-Coated Carbon Nanotubes for Highly Efficient Enrichment of Uranium(VI).
ACS Omega
December 2024
School of Earth and Environment, Anhui University of Science and Technology, Huainan 232001, P. R. China.
A strategically designed ternary nanohybrid (TNS-PDA/CNT), consisting of titanate nanosheet (TNS) and polydopamine-modified multiwalled carbon nanotube (PDA/CNT composite), was synthesized by the facile hydrothermal method and wet impregnation method for removal of U(VI) from aqueous solution and were characterized by transmission electron microscopy (TEM), scanning electron microscopy-energy-dispersive X-ray spectroscopy (SEM-EDS), X-ray diffraction (XRD), Fourier transform infrared (FT-IR), thermogravimetric analysis (TGA), Raman spectroscopy, Brunauer-Emmett-Teller (BET), and X-ray photoelectron spectroscopy (XPS). TNSs were introduced into the PDA/CNT composite, which effectively averted the agglomeration of the CNT and further exposed more adsorption sites. PDA thin layer exposing more active sites was conducive to enhance adsorption capacity and kinetic.
View Article and Find Full Text PDFDesigned functions of oxide/hydroxide nanosheets elemental replacement/doping.
Chem Soc Rev
October 2024
School of Energy Science and Engineering, Vidyasirimedhi Institute of Science and Technology (VISTEC), 555 Moo 1, Payupnai, Wangchan, Rayong 21210, Thailand.
Partial replacement of one structural element in a solid with another of a similar size was conducted to impart functionality to the solids and modify their properties. This phenomenon is found in nature in coloured gemstones and clay minerals and is used in materials chemistry and physics, endowing materials with useful properties that can be controlled by incorporated heteroelements and their amounts. Depending on the area of research (or expected functions), the replacement is referred to as "isomorphous substitution", "doping", Herein, elemental replacement in two-dimensional (2D) oxides and hydroxides (nanosheets or layered materials) is summarised with emphasis on the uniqueness of their preparation, characterisation and application compared with those of the corresponding bulk materials.
View Article and Find Full Text PDFUltrahydrophilic Inorganic Nanosheet-Based Nanofiltration Membranes for High Efficiency Separations of Inorganic Salts and Organic Dyes.
Langmuir
October 2024
Department of Advanced Materials Science, Faculty of Engineering and Design, Kagawa University, 2217-20 Hayashi-cho, Takamatsu-shi 761-0396, Japan.
Two-dimensional (2D) inorganic nanomaterials have garnered extensive attention in the fabrication of inorganic nanofiltration membranes due to their unique structures and properties. In this study, we developed a facile process for fabricating large-scale ultrahydrophilic nanofiltration membranes using layered titanate HTiO·HO nanosheets (HT-ns). A drying deposition process was used to fabricate HT-ns membranes on a poly(tetrafluoroethylene) (TF) substrate.
View Article and Find Full Text PDFAccelerated Synthesis of TS-2 Zeolite via 2D Heterogeneous Nucleation for Efficient HO Production.
Small
December 2024
Key Laboratory of Advanced Rubber Material, Ministry of Education, Qingdao University of Science and Technology, Qingdao, 266042, China.
MEL type c is crucial for addressing energy and environmental crises, yet efficient synthesis remains a challenge due to thermodynamic and kinetic limitations. In this work, TS-2 as typical zeolite is successfully synthesized with high efficiency (12 h with 92% yield) by introducing titanate acid (TA) 2D nanosheet into a hydrothermal synthesis system. A newly defined TA/TS-2 heterostructure is precisely identified as being incorporated into the zeolite framework via a heterogeneous nucleation mechanism.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!