The impact of focused ion beam induced damage on scanning spreading resistance microscopy measurements.

Scanning Spreading Resistance Microscopy is a well-established technique for obtaining quantitative two- and three-dimensional carrier profiles in semiconductor devices with sub-nm spatial resolution. However, for sub-100 nm devices, the use of focused ion beam becomes inevitable for exposing the region of interest on a sample cross section. In this work, we investigate the impact of the focused ion beam milling on spreading resistance analysis and we show that the electrical effect of the focused ion beam extends far beyond the amorphous region and depends on the dopant concentration, ion beam energy, impact angle, and current density. For example, for dopant concentrations between 1.0 × 10 and 1.5 × 10 cm we observe dopant deactivation at least between 23 and 175 nm for a glancing 30 keV ion beam. Further, we show that dopant deactivation is caused by defect diffusion during milling and is not directly impacted by the presence of Gallium in the sample. Later, we also discuss potential ways to mitigate these effects.