Epitaxial growth and structure of cobalt ferrite thin films with large inversion parameter on Ag(001).

Cobalt ferrite ultrathin films with the inverse spinel structure are among the best candidates for spin filtering at room temperature. High-quality epitaxial CoFeO films about 4 nm thick have been fabricated on Ag(001) following a three-step method: an ultrathin metallic CoFe alloy was first grown in coherent epitaxy on the substrate and then treated twice with O, first at room temperature and then during annealing. The epitaxial orientation and the surface, interface and film structure were resolved using a combination of low-energy electron diffraction, scanning tunnelling microscopy, Auger electron spectroscopy and in situ grazing-incidence X-ray diffraction. A slight tetragonal distortion was observed, which should drive the easy magnetization axis in-plane due to the large magneto-elastic coupling of such a material. The so-called inversion parameter, i.e. the Co fraction occupying octahedral sites in the ferrite spinel structure, is a key element for its spin-dependent electronic gap. It was obtained through in situ resonant X-ray diffraction measurements collected at both the Co and Fe K edges. The data analysis was performed using FDMNES, an ab initio program already extensively used to simulate X-ray absorption spectroscopy, and shows that the Co ions are predominantly located on octahedral sites with an inversion parameter of 0.88 (5). Ex situ X-ray photoelectron spectroscopy gives an estimation in accordance with the values obtained through diffraction analysis.