Experimental Analysis of the Quality of Needle-Assisted Fenestration in Aortic Stent-Grafts and the Differences Between Gradual and Rapid Balloon Dilation.

To report the findings of an in vitro experiment to evaluate the quality of needle fenestrations dilated by different size balloons in various stent-grafts and to investigate the differences between gradual and rapid dilation. Fenestrations were made using an 18-G needle in 5 different polyester or expanded polytetrafluoroethylene (ePTFE) stent-grafts: Relay, Valiant, Hercules, TAG, and Ankura. Each stent-graft received 2 groups of fenestrations: one was followed by gradual sequential dilation (4-, 6-, 8-, and 10-mm balloons) and the other by rapid dilation (4- and 10-mm balloons). The pressure was increased to 10 atmospheres or until the balloon was fully inflated with no waist. Quantitative and qualitative evaluations, including fenestration diameter, area, shape, and margins were conducted using light microscopy and scanning electron microscopy. Relay had the strongest resistance to dilation and Ankura the slightest. The maximum length and area of holes expanded as the balloon diameter increased. The fenestrations in polyester devices were mostly elliptical or slit-like, with limited tears but extensive fibers visible in the margin, while ePTFE stent-grafts showed larger fenestration areas with clearer margins. Ankura showed the best quality of fenestrations, which were always circular or square without fabric tears, while the holes in the TAG were square or elliptical but sometimes had a slit after large balloon dilation (≥6 mm). The Relay, Valiant, Hercules, and Ankura devices showed no difference in maximum diameter, fenestration area, or scores of shape and margin (p>0.05). Rapid dilation in the TAG increased the rate of uncontrolled fabric tear, resulting in a larger final diameter (12.90 vs 10.82 mm, p=0.047), smaller area (30.46 vs 41.09 mm, p=0.028), worse shape (0.75 vs 1.20, p=0.268), and worse margin (0.40 vs 1.00, p=0.174). Though the decreased fenestration shape and margin scores did not reach statistical significance, the trend for decline was more obvious than with the other devices. Materials and structures of the stent-grafts determine the quality of fenestrations dilated by different size balloons. The use of sequential vs rapid balloon dilation is also crucial for fashioning high-quality fenestrations and should be selected judiciously.