Biomass waste contributes 14% of the total global energy. And 15-20% of the coal-fine waste from coal mines are deposited in the rivers, ponds, etc., unused, which leads to resource wastage and environmental pollution. The present study aims utilizing biomass and coal-fine waste for producing biomass-coal briquettes without using a binding material. Three different average sizes 50, 134.3, and 199.7 μm of biomass mixture (bagasse, groundnut shell, and woodchips) and coal-fines were used to make different ratios of biomass and coal mixture briquettes. Then, it is subjected to proximate, scanning electron microscope/elemental (SEM/EDX) and thermo-gravimetric analysis (TGA) to understand its property. Proximate analysis results revealed that the biomass waste has the low ash, sensible fixed carbon, and high volatile matter content. A briquette of biomass: coal = 7:1 ratio 50-μm particle size case was chosen for SEM/EDX and TGA analysis since it holds reasonable fixed carbon value comparatively. SEM analysis revealed irregular surfaces, cracks, cavities and longitudinal cracks, veins distribution all around, ups and shallows on the surface and it is the most favorable condition for fuel combustion since oxidant reaches the core of the fuel with less resistant. TGA reconfirms the spontaneous burning characteristics of the entire volatiles and fixed carbon. EDX analysis shows that the carbon and potassium are the two major elements present in the tested briquettes.
Biomass waste contributes 14% of the total global energy. And 15-20% of the coal-fine waste from coal mines are deposited in the rivers, ponds, etc., unused, which leads to resource wastage and environmental pollution.
Coal processing industries generate millions of tons of fines (<3 mm) during mining operation and are often considered as wastes. These wastes have enormous potential in serving as energy and metallurgical operation feedstock. One avenue for its use is densification into briquettes or pelletizes.
Polyacrylamide grafted oatmeal (OAT-g-PAM) was synthesized by conventional method. The grafting of the PAM chains on the biomaterial backbone was confirmed through intrinsic viscosity study, FTIR spectroscopy, elemental analysis (C, H, N, S and O), SEM morphology and TGA study. The intrinsic viscosity of oatmeal appreciably improved on grafting of PAM chains, thus resulting grafted product with potential application as superior viscosifier.