Synthesis, Cr(VI) removal performance and mechanism of nanoscale zero-valent iron modified potassium-doped graphitic carbon nitride.

A novel composite (nZVI@K-GCN) was firstly synthesized by liquid phase reducing nanoscale zero-valent iron (nZVI) on potassium-doped graphitic carbon nitride (K-GCN). The results of Fourier transform infrared (FTIR) spectrometry, X-ray diffraction (XRD), scanning electron microscopy (SEM) and Brunauer-Emmett-Teller (BET) suggested that nZVI@K-GCN possessed abundant active functional groups such as terminal amino-groups (-NH or -NH groups) and -OH, and the specific surface area and pore volume from BET of nZVI@K-GCN were 4.7 times and 3.7 times higher than that of graphitic carbon nitride (GCN), respectively. These properties showed that the composite was especially suitable for heavy metal treatment. The application of the composite in the removal of chromium(VI) from aqueous solution showed that the maximum adsorption capacity of nZVI@K-GCN towards Cr(VI) was 68.6 mg/g at 308 K when the initial concentration of Cr(VI) was 30 mg/L, and more than 99% removal was obtained at pH = 3. This adsorption was an endothermic and spontaneous process. XPS patterns and batch experiments proved that complexation, electrostatic attraction and reduction precipitation were the main adsorption mechanism for Cr(VI) on nZVI@K-GCN.