Purpose: The aim of this study was to evaluate the clinical performance and reliability of plasma sprayed nanostructured zirconia (NSZ) coating.
Materials And Methods: This study consisted of three areas of analysis: (1) Mechanical property: surface roughness of NSZ coating and bond strength between NSZ coating and titanium specimens were measured, and the microstructure of bonding interface was also observed by scanning election microscope (SEM). (2) Biocompatibility: hemolysis tests, cell proliferation tests, and rat subcutaneous implant test were conducted to evaluate the biocompatibility of NSZ coating. (3) Mechanical compatibility: fracture and artificial aging tests were performed to measure the mechanical compatibility of NSZ-coated titanium abutments.
Results: In the mechanical study, 400 µm thick NSZ coatings had the highest bond strength (71.22 ± 1.02 MPa), and a compact transition layer could be observed. In addition, NSZ coating showed excellent biocompatibility in both hemolysis tests and cell proliferation tests. In subcutaneous implant test, NSZ-coated plates showed similar inflammation elimination and fibrous tissue formation processes with that of titanium specimens. Regarding fatigue tests, all NSZ-coated abutments survived in the five-year fatigue test and showed sufficient fracture strength (407.65-663.7 N) for incisor teeth.
Conclusion: In this study, the plasma-sprayed NSZ-coated titanium abutments presented sufficient fracture strength and biocompatibility, and it was demonstrated that plasma spray was a reliable method to prepare high-quality zirconia coating.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC7314630 | PMC |
| http://dx.doi.org/10.4047/jap.2020.12.3.157 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
[Application value of excimer laser ablation combined with drug-coated balloon in non-stent atherosclerotic lesions of lower extremity arteries].
Zhonghua Wai Ke Za Zhi
December 2022
Department of Vascular Surgery, Zhongshan Hospital, Fudan University; National Clinical Research Center for Interventional Medicine, Shanghai 200032, China.
To examine the effect of excimer laser ablation (ELA) combining with drug-coated balloon (DCB) for atherosclerotic lesions in no-stenting zones (NSZ) of the lower extremity. From June 2019 to December 2021, 46 patients who underwent ELA combining with DCB in lesions of NSZ at Zhongshan Hospital, Fudan University and Jinshan Hospital, Fudan University were retrospectively enrolled, including 29 males and 17 females. The age was (72.
View Article and Find Full Text PDFThe biocompatibility and mechanical properties of plasma sprayed zirconia coated abutment.
J Adv Prosthodont
June 2020
Shandong Provincial Key Laboratory of Oral Tissue Regeneration, School of Stomatology, Shandong University, Jinan, Shandong Province, China.
Purpose: The aim of this study was to evaluate the clinical performance and reliability of plasma sprayed nanostructured zirconia (NSZ) coating.
Materials And Methods: This study consisted of three areas of analysis: (1) Mechanical property: surface roughness of NSZ coating and bond strength between NSZ coating and titanium specimens were measured, and the microstructure of bonding interface was also observed by scanning election microscope (SEM). (2) Biocompatibility: hemolysis tests, cell proliferation tests, and rat subcutaneous implant test were conducted to evaluate the biocompatibility of NSZ coating.
The aim was to investigate the osseointegration of a novel coating-plasma-sprayed nanostructured zirconia (NSZ) in dental implant. Nanostructured zirconia coating on non-thread titanium implant was prepared by plasma spraying, the implant surface morphology, surface roughness and wettability were measured. In vivo, nanostructured zirconia-coated implants were inserted in rabbit tibia and animals were respectively sacrificed at 2, 4, 8 and 12 weeks after implantation.
View Article and Find Full Text PDFNanostructured films of amphiphilic fluorinated block copolymers for fouling release application.
Langmuir
November 2008
Dipartimento di Chimica e Chimica Industriale and UdR Pisa INSTM, Universita di Pisa, via Risorgimento 35, 56126 Pisa, Italy.
New amphiphilic block copolymers S nSz m consisting of blocks with varied degrees of polymerization, n and m, of polystyrene, S, and polystyrene carrying an amphiphilic polyoxyethylene-polytetrafluoroethylene chain side-group, Sz, were prepared by controlled atom transfer radical polymerization (ATRP). The block copolymers, either alone or in a blend with commercial SEBS (10 wt% SEBS), were spin-coated in thinner films (200-400 nm) on glass and spray-coated in thicker films ( approximately 500 nm) on a SEBS underlayer (150-200 microm). Angle-resolved X-ray photoelectron spectroscopy (XPS) measurements proved that at any photoemission angle, varphi, the atomic ratio F/C was larger than that expected from the known stoichiometry.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!