Nano-purification of raw semen minimises oxidative stress with improvement in post-thaw quality of buffalo spermatozoa.

The study consisted of application of anti-ubiquitin antibodies (Abs)-coated iron oxide-nanoparticles (IONPs) for minimisation of oxidative stress to contemporary live spermatozoa from the raw semen. Round-shaped IONPs (12.09 ± 0.91 nm) after two-stage functionalisation (silanisation and pegylation) were conjugated with Abs. Four aliquots from each of the 24 ejaculates (4 buffalo bulls) formed Control (Group I) and treatment (II, III and IV) groups; each containing 150 ± 25 million dead/damaged spermatozoa. IONPs-Abs complex were added at ratio of 1:1 (0.5 µg/ml), 1:2 (1.0 µg/ml) and 1:4 (2.0 µg/ml), respectively, in Groups II, III and IV. The semen quality parameters showed improvement at lag-stage (post-nano-purification before processing for cryopreservation). The mean post-thaw motility (%) in Group IV was found to be greater (p < .05) than Group I. Moreover, the overall DNA integrity (%) at post-thaw stage was improved in the nano-purified semen samples. The value of malondialdehyde was greater (p < .001) in Group I than Groups II, III and IV. The mean total antioxidant capacity and superoxide dismutase (U/mg protein) activity values in Group IV was greater (p < .05) than Group I. The study results show that IONPs conjugated with anti-ubiquitin Abs at 2.0 µg/ml can be an effective dose for depletion of dead/damaged spermatozoa from buffalo ejaculates to minimise oxidative stress.