Concentration-dependent effects of latex F1-protein fraction incorporated into deproteinized bovine bone and biphasic calcium phosphate on the repair of critical-size bone defects.

F1-protein fraction (F1) is a natural bioactive compound extracted from the rubber tree, Hevea brasiliensis, and has been recently studied for its therapeutic potential in wound healing. In this study, we investigated the concentration-dependent effects of F1 (0.01%, 0.025%, 0.05%, and 0.1%) incorporated into deproteinized bovine bone (DBB) and porous biphasic calcium phosphate (pBCP), on the repair of rat calvarial critical-size bone defects (CSBD). The defects were analyzed by 3D-microtomography and 2D-histomorphometry at 12 weeks postsurgery. The binding efficiency of F1 to pBCP (96.3 ± 1.4%) was higher than that to DBB (67.7 ± 3.3%). In vivo analysis showed a higher bone volume (BV) gain in all defects treated with DBB (except in 0.1% of F1) and pBCP (except in 0.05% and 0.1% of F1) compared to the CSBD without treatment/control group (9.96 ± 2.8 mm ). DBB plus 0.025% F1 promoted the highest BV gain (29.7 ± 2.2 mm , p < .0001) compared to DBB without F1 and DBB plus 0.01% and 0.1% of F1. In the pBCP group, incorporation of F1 did not promote bone gain when compared to pBCP without F1 (15.9 ± 4.2 mm , p > .05). Additionally, a small BV occurred in defects treated with pBCP plus 0.1% F1 (10.4 ± 1.4 mm p < .05). In conclusion, F1 showed a higher bone formation potential in combination with DBB than with pBCP, in a concentration-dependent manner. Incorporation of 0.25% F1 into DBB showed the best results with respect to bone formation/repair in CSBD. These results suggest that DBB plus 0.25% F1 can be used as a promising bioactive material for application in bone tissue engineering.