Objective: The aim of this study was to compare both the elastic modulus (EM) and the flexural strength (FS) of two materials used in dental prosthesis, namely polymethylmethacrylate (PMMA) and polymethylmethacrylate reinforced with graphene (G-PMMA).
Materials And Methods: Twenty rectangular samples were manufactured by a milling machine and divided into two groups (n= 10/group): Group 1, PMMA; Group 2, G-PMMA. The specimens were subjected to a three-point bending test conducted in the elastic range to evaluate EM. A similar test was protracted until fracture to evaluate FS. Data on EM and FS were statistically analyzed with independent-samples t-test in order to compare the two groups. A scanning electron microscope (SEM) (5.00 kx and 1.00 kx magnification) was used to evaluate the morphology of sample's fracture.
Results: Compared to PMMA samples, each G-PMMA sample showed significantly higher values of FS (p <0.001) and EM (p <0.001). SEM images analysis showed an inhomogeneous fracture morphology in G-PMMA samples.
Conclusions: The results show that G-PMMA is a promising material to be used for prosthetic purposes. This is demonstrated by a significant increase in both peak load and bending stiffness, resulting from the bending test performed on G-PMMA samples. Furthermore, the latter exhibit greater homogeneity in their mechanical behavior, supporting the potential value of this material in dental prosthesis.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.26355/eurrev_202005_21301 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Effect of boiling water soaking on the mechanical properties and durability of nanoclay-enhanced bamboo and glass fiber epoxy composites.
Sci Rep
January 2025
Department of Mechanical and Industrial Engineering, Manipal Institute of Technology, Manipal Academy of Higher Education, Manipal, 576104, India.
Fiber-reinforced polymer composites are subjected to harsh environmental conditions over the course of their designed lifespan. Studying the aging process of fiber-reinforced polymer composites exposed to boiling water is critical for improving their durability. This study uses a hand lay-up technique to fabricate composites from glass fiber, bamboo fiber, nanoclay, and epoxy.
View Article and Find Full Text PDFMechanical properties of modern restorative "bioactive" dental materials - an in vitro study.
Sci Rep
January 2025
Department of General Dentistry, Medical University of Lodz, 251 Pomorska Str, Lodz, 92-213, Poland.
This study aimed at assessing the mechanical properties and degradation of commercial bioactive materials. The bioactive materials (Activa Bioactive Restorative, Beautifil Flow Plus F00, F03, Predicta Bulk Bioactive) and composite resin Filtek Supreme Flow were submitted to flexural and diametral tensile strength tests (FS, DTS), modulus of elasticity (ME) evaluation, and analysis of aging in 70% ethanol and saliva on their hardness and sorption. The results for DTS ranged from 33.
View Article and Find Full Text PDFUnderwater Superoleophobic and Transparent Films with Mechanical Robustness and High Durability in Harsh Environments.
ACS Appl Mater Interfaces
January 2025
Key Laboratory of Advanced Technology for Materials Synthesis and Processing, School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China.
Underwater superoleophobic and transparent (UST) films are promising in applications, such as advanced optical devices in marine environments. However, the mechanical robustness and durability in harsh environments of the existing UST films are still unsatisfactory. In this work, we present a free-standing nacre-inspired mineralized UST (NIM-UST) film with high aragonite content and excellent mechanical properties toward robust underwater superoleophobicity on two surfaces and transparency (94%) in harsh seawater environments.
View Article and Find Full Text PDFWaste marble sludge and calcined clay brick powders in conventional cement farina production for cleaner built environment.
Sci Rep
January 2025
Center for Global Health Research, Saveetha Institute of Medical and Technical Sciences, Saveetha University, Chennai, India.
In the manufacturing of some sectors, such as marble and brick, certain byproducts, such as sludge, powder, and pieces containing valuable chemical compounds, emerge. Some concrete plants utilize these byproducts as mineralogical additives in Turkey. The objective of the experimental study is to ascertain whether the incorporation of waste from the marble and brick industries, in powder form, into cement manufacturing as a mineralogical additive or substitute is a viable option.
View Article and Find Full Text PDFEnhanced mechanical properties and in vitro bioactivity of silicon nitride ceramics with SiO, YO, and AlO as sintering aids.
J Mech Behav Biomed Mater
January 2025
School of Materials Science and Engineering, University of Jinan, Jinan, 250022, China. Electronic address:
Silicon nitride (Si₃N₄) ceramics exhibit excellent mechanical properties and biocompatibility, making them highly suitable for biomedical applications, particularly in implants. In this study, the mechanical properties and bioactivity of Si₃N₄ ceramics with varying amounts of Y₂O₃-Al₂O₃-SiO₂ sintering aids were investigated. Increasing the sintering additive content from 4 wt% to 8 wt% substantially improved the bulk density of the ceramics, leading to notable enhancements in mechanical properties.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!