Synthesis and Characterization of Fluoridated Silver Nanoparticles and Their Potential as a Non-Staining Anti-Caries Agent.

Objectives: The first objective of this study was to prepare sodium fluoride (NaF) solution with various concentrations of polyethylene glycol-coated silver nanoparticles (PEG-AgNPs). The second objective was to study the antibacterial activity against and the tooth-staining effect of the solution.

Methods: PEG-AgNPs were prepared via the one-step chemical reduction of silver acetate with thiolated polyethylene glycol. The PEG-AgNPs were characterized with ultraviolet-visible spectrometry and transmission electron microscopy. The half maximal inhibitory concentration (IC50) for the PEG-AgNPs against and human gingival fibroblasts (HGF-1) were determined. The staining effect on dentin and enamel for the 2.5% NaF solutions with PEG-AgNPs at 12,800, 6400, 1600, and 400 ppm was investigated using digital spectrophotometry. The IC50 of the fluoridated silver nanoparticles against were measured.

Results: The PEG-AgNPs have an average diameter of 2.56±0.43 nm and showed excellent stability at high ionic strength (2.5% NaF) for 18 months. The IC50 of PEG-AgNPs against was found to be 21.16±1.08 ppm silver, which was half of IC50 against HGF-1 cells (42.36±1.12 ppm), providing a working range to kill bacteria with no harm to human cells. The formulations with different concentrations of PEG-AgNPs showed no significant staining of teeth. Combining PEG-AgNPs with NaF significantly expanded the therapeutic window against by reducing its IC50.

Conclusion: A biocompatible solution of NaF with PEG-AgNPs was developed. Because it has antibacterial activity against and no tooth-staining effect, it can be used as an anti-caries agent.