Tailoring the Vertical Morphology of Organic Films for Efficient Planar-Si/Organic Hybrid Solar Cells by Facile Nonpolar Solvent Treatment.

The optical and electrical properties of the blending organic film poly(3,4-ethylenedioxy-thiophene):poly(styrenesulfonate) (PEDOT:PSS) are strongly affected by its morphology, resulting in the performance variation in Si/organic hybrid solar cells. Here, a facile postsolvent treatment is used to tailor the vertical morphology of PEDOT:PSS by introducing a nonpolar solvent. X-ray photoelectron spectroscopy depth-profiling measurements show that the distribution of PEDOT and PSS on the surface of n-type Si can be changed by nonpolar solvent -hexane (NHX) treatment, where more PSS aggregate at the bottom of the blend film and more PEDOT float up to the top, as compared with the reference sample. As a result, after NHX treatment, the average lifetime of the Si/organic films is increased from 152 μs for untreated samples to 248 μs for NHX-treated ones because of the better passivation effect of PSS on Si. Moreover, the transmission line model measurements indicate that the contact resistance () of PEDOT:PSS film and the Ag electrode is decreased for better charge collection after NHX treatment. Eventually, the best power conversion efficiency (PCE) of 13.78% for NHX-treated planar solar cells is obtained, much higher than the PCE (with best of 12.78%) of reference devices without nonpolar solvent treatment. Our results provide a facile method to tailor the vertical morphology of the PEDOT:PSS in Si/organic hybrid solar cells.