Extreme Foaming Modes for SCF-Plasticized Polylactides: Quasi-Adiabatic and Quasi-Isothermal Foam Expansion.

The experimental evidence on depressurization foaming of the amorphous D,L-polylactide, which is plasticized by subcritical (initial pressures below the critical value) or supercritical (initial pressures above the critical value) carbon dioxide at a temperature above the critical value, relates to two extreme cases: a slow quasi-isothermal foam expansion, and a rapid quasi-adiabatic expansion. Under certain conditions, the quasi-isothermal mode is characterized by the non-monotonic dependencies of the foam volume on the external pressure that are associated with the expansion-to-shrinkage transition. The quasi-adiabatic and quasi-isothermal expansions are characterized by a significant increase in the degree of foam expansion under conditions where the CO initial pressure approaches the critical value. The observed features are interpreted in terms of the energy balance in the foam volume and the phenomenological model based on the equation of the foam state. The expansion-to-shrinkage condition is based on the relationship between the average bubble radius and the pressure derivative of the surface tension for the plasticized polylactide. The maximum expansion ratio of the rapidly foamed polylactide in the vicinity of the critical point is interpreted in terms of the maximum decrement of the specific internal energy of the foaming agent (carbon dioxide) in the course of depressurization.