Purpose: To assess the influence of ferrule thickness on the fracture resistance and failure mode of endodontically treated bovine incisors and to predict the long-term prognosis, as well as choose the most suitable clinical treatment, for teeth with different ferrule thicknesses.
Materials And Methods: A total of 50 endodontically treated bovine incisors were restored with quartz fiber posts and metal crowns and separated into five groups (n = 10 each): no ferrule (group A); 0.5-mm-thick ferrule (group B); 1.0-mm-thick ferrule (group C); 1.5-mm-thick ferrule (group D); and 2.0-mm-thick ferrule (group E). All specimens were subjected to a fatigue loading test (2.33 Hz, 50 N, 300,000 cycles). Survived specimens were loaded until fracture on a universal testing machine at an angle of 135 degrees and a crosshead speed of 0.5 mm/minute. Failure modes and fracture resistance were recorded. Data were analyzed using one-way ANOVA and least significant difference tests.
Results: A significant increase (P < .05) was detected in fracture resistance with increase in ferrule thickness. Group D (1.5 mm) and group E (2.0 mm) showed significantly higher fracture resistance than the other three groups. All failures belonged to restorable fracture patterns.
Conclusion: Ferrule thickness contributed significantly to the fracture resistance of endodontically treated bovine incisors restored with quartz fiber posts and metal crowns. Teeth with ferrule thickness of ≥ 1.5 mm can achieve higher fracture resistance and have a better long-term prognosis.
Download full-text PDF |
Source |
|---|---|
| http://dx.doi.org/10.11607/ijp.6423 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Fracture resistance of analog and CAD-CAM long-span fixed provisional restorations: An in vitro experimental study.
J Prosthodont
January 2025
The Office of Assistant Dean for Research, School of Dental Medicine, Medical Sciences Campus, University of Puerto Rico, San Juan, Puerto Rico.
Purpose: This study aimed to evaluate and compare the fracture resistance of long-span fixed provisional restorations fabricated using milling, three-dimensional (3D) printing, and conventional methods.
Materials And Methods: Sixty specimens were prepared, divided into four groups of 15 each, corresponding to four fabrication methods: computer-aided design and computer-aided manufacturing (CAD-CAM) milled provisional resins, 3D-printed provisional resins, 3D-printed permanent resins, and conventional bis-acryl restorations reinforced with wire. The specimens underwent a three-point bending test using a universal testing machine to measure fracture resistance, quantified as maximum force (in Newtons).
The cumulative exposure to triglyceride-glucose index and the risk of onset fragility fractures.
Bone
January 2025
The School of Public Health, North China University of Science and Technology, Tangshan, Hebei, China. Electronic address:
Objective: To investigate the association between the cumulative exposure to triglyceride-glucose index (cumTyG index) and fragility fractures in the general population.
Methods: This prospective cohort study analyzed active and retired employees of Kailuan Group who participated in three consecutive health examinations in 2006, 2008 and 2010, and were followed up until 31st December 2022. The cohort comprised 55,824 participants who met the inclusion and exclusion criteria and were grouped using the cumTyG index quartiles.
Effectiveness of a New Device for Hand, Wrist, and Forearm Rehabilitation: Feasibility Randomized Controlled Trial.
JMIR Rehabil Assist Technol
January 2025
Department of Occupational Therapy, Faculty of Rehabilitation Medicine, University of Alberta, Edmonton, AB, Canada.
Background: Forearm, wrist, and hand impairments affect many individuals and impose a significant economic burden on health care systems. The FEPSim (flexion, extension, pronation, and supination) is designed for hand and wrist rehabilitation. It could become part of the standard care for upper extremity rehabilitation, aiming to improve range of motion, dexterity, and strength during therapeutic activities.
View Article and Find Full Text PDFThe Posterior Ligamentous Complex: Anatomic and Biomechanical Considerations in Injury Classification and Management.
J Am Acad Orthop Surg
January 2025
From the Department of Orthopaedics (A. Mo and F. Mo), Medstar Georgetown University Hospital, Washington, DC, and the Department of Orthopaedic Surgery (S. Lockey), University of Virginia, Charlottesville, VA.
The posterior ligamentous complex (PLC) provides critical structural support in the thoracolumbar spine. Its role in resisting progressive flexion is particularly important at the thoracolumbar junction due to the transition from the rigid thoracic spine to the more mobile lumbar region. Each component of the PLC contains anatomic features that contribute to both the structure and function of the PLC as a whole.
View Article and Find Full Text PDFEffect of pulp-chamber lateral wall thickness and number on fracture resistance in endocrown-restored molars: An in vitro study.
J Dent Sci
January 2025
Department of Cariology and Endodontology, Peking University School and Hospital of Stomatology, Beijing, China.
Background/purpose: It remains unclear how the thickness and number of pulp-chamber lateral walls (PCLWs) affects fracture resistance in endocrown-restored teeth.
Materials And Methods: 64 mandibular molars were collected and randomly divided into eight groups (n = 8). In group C (control group), the teeth were untreated.
Want AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!