Mitigation the release of toxic PH and the fire hazard of PA6/AHP composite by MOFs.

Aluminum hypophosphite (AHP) is a high-efficiency phosphorus-based flame retardant with high P content, which is widely used in Polyamide 6 (PA6). However, AHP releases phosphine gas (PH) at high temperatures, which is highly toxic to human's health and environment. Metal-organic frameworks (MOFs) have porous structure exhibiting high performance in gas adsorption. Therefore, mesoporous iron (III) carboxylate [MIL-100 (Fe)] was synthesized in this work and employed to study the adsorption capacity of toxic PH in PA6/AHP composite during processing. AHP was combined with melamine cyanurate (MCA) and MIL-100 (Fe) followed by blending with PA6 to prepare PA6 composites (PA6/MA and PA6/MAF). PA6/MAF with the weight ratio of 5:5 performed well in inhibiting the release of PH during the processing of composite as well as the accelerated thermal experiment devised by our group. Besides, PA6/MAF (5:5) showed relatively low fire hazard reflected by the reduction of the peak of heat release rate of PA6 composite from 962 to 260 kW/m compared with that of pure PA6 in the cone calorimeter test, and MIL-100 (Fe) along with MCA also presented synergistic effect in suppressing the emission of carbon monoxide. The subtle selection of MOFs herein has the potential to be used as a promising synergist for hazardous gases released from polymer composites to improve the occupational and fire safety in the society.