Comparative evaluation among laser-treated, machined, and sandblasted/acid-etched implant surfaces: an in vivo histologic analysis on sheep.

Purpose: The aim of the present in vivo analysis was to evaluate the osseointegration process of titanium implants with three different surfaces (machined, sandblasted and acid-etched, and laser-treated) after 15 and 30 days of healing period.

Materials And Methods: Thirty-six implants with different surfaces were placed in the iliac crest of four Bergamasca sheep. The implant surfaces tested were sandblasted and acid-etched (group A), laser-treated (group B), and fully machined (group C). Two animals were sacrificed after 15 days while the other two after 30 days. Histological and histomorphometric analyses were performed.

Results: After 30 days, the bone tissue layer onto implant groups A and B appeared almost continuous with small marrow spaces interruption, while on the machined surface (group C), larger spaces with marrow tissue alternated with the bony trabeculae onto the titanium surface. Implants in groups A and B showed significantly higher implant contact percentage (BIC%) value than group C (P < 0.05). Moreover, it was observed a BIC% increase in both groups A and B between 15 and 30 days while in the machined group (group C), the BIC% decreased.

Conclusion: Results from the present in vivo analysis revealed that both sandblasted/acid-etched and laser-treated titanium implants, compared to the machined ones, have higher values of osseointegration in less healing time.