Thio-urethane oligomers improve conversion and mechanical properties of resin cements. The objective of this study was to evaluate the effect of resin cements formulated with thio-urethane (TU) oligomers on microtensile bond strength (µTBS) of ceramics to composites subjected to thermal/mechanical cycling. BisGMA/UDMA/TEGDMA (50/30/20 wt%) containg 0 (control, EC) or 20 wt% aliphatic or aromatic thiourethane (HDDI and BDI, respectively) were mixed with CQ/amine (0.2/0.8 wt%) and 25 wt% 0.7um Ba glass. Rely X Ultimate (RU-3M ESPE) was used as the commercial control. The cements were sandwiched between ceramic (IPS e.max Press) and resin composite blocks (Filtek Supreme, 3 M-ESPE). Eight bonded blocks were produced per experimental group. Prior to bonding, ceramic surfaces were etched (20 s - 10% HF) and silanized. Composite surfaces were treated with Single Bond Universal (3 M ESPE). Specimens were stored for 24 h in distilled water at 37 °C, and then either tested immediately, or subjected to thermal (10,000, 5 °C and 55 °C) or mechanical cycling (300,000 cycles). Sticks (1 mm, average of 25 sticks per block) were cut and tested for µTBS (1.0 mm/min). Data were analyzed with two-way ANOVA/Tukey's test ( = 5%). Fracture surfaces were analyzed to determine failure modes. The µTBS for HDDI and RU was significantly higher than BDI and EC cements. BDI led to significantly higher µTBS than EC after 24 h, Tc and Mf. µTBS decreased significantly after thermal/mechanical cycling for all groups. Failure modes were predominantly adhesive or mixed. The use of selected thio-urethane oligomers was able to increase the µTBS of composite-cement-ceramic specimens. Tc and Mf reduced µTBS for all resins cements.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC6964779 | PMC |
| http://dx.doi.org/10.1080/26415275.2019.1693274 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Objectives: Thio-urethane oligomeric additives have been shown to improve the mechanical properties of dental composites and resin cements. To try to harness those same properties in dental adhesives, in this study, these oligomers (TU) were added to the matrix and/or as filler functionalization of experimental adhesives, and the effects on conversion and mechanical properties were analyzed.
Methods: BisGMA and HEMA (60/40 wt%) were used as the monomer matrix, made polymerizable by the addition of 0.
Objective: The aim of this in vitro study was to test the effect of different composite modulation protocols (pre-heating, light-curing time and oligomer addition) for bulk filling techniques on resin polymerization stress, intra-pulpal temperature change and degree of conversion.
Methods: Class I cavities (4mm depth×5mm diameter) were prepared in 48 extracted third molars and divided in 6 groups. Restorations were completed with a single increment, according to the following groups: (1) Filtek Z250XT (room temperature - activated for 20s); (2) Filtek Z250XT (at room temperature - activated for 40s); (3) Filtek Z250XT (pre-heated at 68°C - activated for 20s); (4) Filtek Z250XT (pre-heated at 68°C - activated for 40s); (5) Filtek BulkFill (at room temperature - activated for 20s); (6) Filtek Z250XT (modified by the addition of a thio-urethane oligomer at room temperature - activated for 40s).
Effect of experimental resin cements containing thio-urethane oligomers on the durability of ceramic-composite bonded interfaces.
Biomater Investig Dent
November 2019
School of Dentistry, Biomaterials and Biomechanics, Oregon Health and Science University, Portland, Oregon.
Thio-urethane oligomers improve conversion and mechanical properties of resin cements. The objective of this study was to evaluate the effect of resin cements formulated with thio-urethane (TU) oligomers on microtensile bond strength (µTBS) of ceramics to composites subjected to thermal/mechanical cycling. BisGMA/UDMA/TEGDMA (50/30/20 wt%) containg 0 (control, EC) or 20 wt% aliphatic or aromatic thiourethane (HDDI and BDI, respectively) were mixed with CQ/amine (0.
View Article and Find Full Text PDFOptical properties and colorimetric evaluation of resin cements formulated with thio-urethane oligomers.
J Esthet Restor Dent
March 2019
Department of Biomaterials and Biomechanics, Oregon Health & Science University, Portland, Oregon.
Objective: The aim of this study was to evaluate the color parameters and optical properties of resin cements (RCs) formulated with thio-urethanes (TUs).
Materials And Methods: Six TUs were synthesized by combining thiols (pentaerythritol tetra-3-mercaptopropionate [PETMP] or trimethylol-tris-3-mercaptopropionate [TMP]) with di-functional isocyanates (1,6-Hexanediol-diissocyante [HDDI] [aliphatic-AL] or 1,3-bis(1-isocyanato-1-methylethyl) benzene [BDI] [aromatic-AR] or Dicyclohexylmethane 4,4'-Diisocyanate [HMDI] [cyclic-CC]). TUs (20 wt%) were added to a BisGMA/UDMA/TEGDMA matrix.
Resin cements formulated with thio-urethanes can strengthen porcelain and increase bond strength to ceramics.
J Dent
June 2018
Department of Biomaterials and Oral Biology, University of São Paulo -USP, São Paulo, Brazil.
Objectives: The use of thio-urethane oligomers has been shown to significantly improve the mechanical properties of resin cements (RCs). The aim of this study was to use thio-urethane-modified RC to potentially reinforce the porcelain-RC structure and to improve the bond strength to zirconia and lithium disilicate.
Methods: Six oligomers were synthesized by combining thiols - pentaerythritol tetra-3-mercaptopropionate (PETMP, P) or trimethylol-tris-3-mercaptopropionate (TMP, T) - with di-functional isocyanates - 1,6-Hexanediol-diissocyante (HDDI) (aliphatic, AL) or 1,3-bis(1-isocyanato-1-methylethyl)benzene (BDI) (aromatic, AR) or Dicyclohexylmethane 4,4'-Diisocyanate (HMDI) (cyclic, CC).