A Study on Blend Ratio-dependent Far-IR and Low-frequency Raman Spectra and WAXD Patterns of Poly(3-hydroxybutyrate)/poly(4-vinylphenol) Using Homospectral and Heterospectral Two-dimensional Correlation Spectroscopy.

An intensive analysis of far-infrared (far-IR), low-frequency Raman, and wide angle X-ray diffraction (WAXD) data has been performed by two-dimensional correlation spectroscopy (2D-COS) as a function of the blend ratio of poly(3-hydroxybutyrate)/poly(4-vinylphenol) (PHB/PVPh). Homospectral 2D-COS revealed that a weak band at 128 cm in the far-IR spectra appeared more clearly in the 2D correlation spectra. Heterospectral 2D-COS (far-IR/low-frequency Raman and far-IR/WAXD) provided very important results that were hardly detected in the conventional 2D-COS. A far-IR peak at 130 cm in the heterospectral 2D-COS had negative correlations with the peaks in the low-frequency Raman spectra at 81, 100, and 110 cm and WAXD profile 8.78 and 11.01°. These results indicated that those peaks have different origins; the 130 cm peak comes from the intermolecular C=O···H-O hydrogen bond between PHB and PVPh, while those for low-frequency Raman and WAXD peaks are the features of PHB crystalline structure.