Bond strength and adhesive interfacial micromorphology of self-adhesive resin cements: Effect of reduced times of pre-etching.

Background: Although acid-etching could increase enamel bond strength of self-adhesive (SA) cements, it may lead to negative effect on dentin. The aim of this study was to assess the effect of shortening of phosphoric acid pre-etching duration on enamel/ dentin shear bond strength (SBS) and interfacial microstructure of Panavia SA Luting Plus (PASA) and Bifix SE (BXSE).

Material And Methods: For both enamel and dentin, effect of pre-etching time was significant (<0.001); however, effect of cement brand and the interaction of two factors was significant only for dentin (p≤0.008). Three pre-etching times increased SBS of both cements to enamel and BXSE to dentin. In case of dentin SBS of PASA, this improvement was significant only for 5 and 10 seconds (<0.001). Adding acid-etching in the three times to both cements similarly improved interfacial adaptation, particularly for enamel.

Results: The evaluations of the biofilm elimination showed results that indicate that the 4% sodium hypochlorite group with positive pressure irrigation presented significant differences with the group that had irrigation with sodium hypochlorite activated with XP-endo Finisher and the chlorhexidine groups to 2% (<0.05).

Conclusions: Interfacial bond strength and adaptation of SA cements used in this study were improved following addition of enamel/dentin etching step for a short time. This was not exceeded for longer times than 5-second. Dentin bond strength, enamel bond strength, pre-etching time, self-adhesive cement.