Evaluation of the Properties, Gas Permeability, and Selectivity of Mixed Matrix Membrane Based on Polysulfone Polymer Matrix Incorporated with KIT-6 Silica.

Mixed matrix membranes (MMMs) separation is a promising technology for gas permeation and separation involving carbon dioxide (CO). However, finding a suitable type of filler for the formation of defect-free MMMs with enhancement in gas permeability remains a challenge. Current study focuses on synthesis of KIT-6 silica and followed by the incorporation of KIT-6 silica as filler into polysulfone (PSF) polymer matrix to fabricate MMMs, with filler loadings of 0-8 wt %. The effect of KIT-6 incorporation on the properties of the fabricated MMMs was evaluated via different characterization techniques. The MMMs were investigated for gas permeability and selectivity with pressure difference of 5 bar at 25 °C. KIT-6 with typical rock-like morphology was synthesized. Incorporation of 2 wt % of KIT-6 into PSF matrix produced MMMs with no void. When KIT-6 loadings in the MMMs were increased from 0 to 2 wt %, the CO permeability increased by ~48%, whereas the ideal CO/CH selectivity remained almost constant. However, when the KIT-6 loading in PSF polymer matrix was more than 2 wt %, the formation of voids in the MMMs increased the CO permeability but sacrificed the ideal CO/CH selectivity. In current study, KIT-6 was found to be potential filler for PSF matrix under controlled KIT-6 loading for gas permeation.