Enhanced antibacterial activity of titanium by surface modification with polydopamine and silver for dental implant application.

Background: Biofilm formation and microbial colonization on the surface of implant devices may cause dental caries and peri-implantitis. Therefore, various surface treatments have been developed to improve the antibacterial activity of titanium implant.

Methods: Silver-loaded polydopamine coating was formed by immersing pure titanium in dopamine hydrochloride/HCl buffer solution for 24 h in 50 mL silver nitrate solutions with different concentrations for 30 min. Microbial growth inhibition and microbial growth curve analyses for bacterial solutions of and incubated with the specimens were respectively conducted by counting the numbers of colonies on agar solid medium and by measuring absorbance using enzyme-linked immunosorbent assay reader.

Results: Silver nanoparticles were uniformly distributed over the whole surface of the polydopamine and silver-coated titanium specimens. The numbers of microbial colonies for both bacteria cultured with surface-modified titanium were significantly lower than those cultured with uncoated titanium. When and were cultured with surface-modified titanium, the lag phase of the growth curves for both bacteria was continually maintained, whereas the lag phase for and changed to exponential phase after 9 and 15 h, respectively, when both bacteria were cultured with uncoated titanium.

Conclusion: It was confirmed that the coating of polydopamine and silver on the surface of titanium effectively retards the microbial growth, which can cause the formation of biofilm and pathogenesis of gum disease in the mouth.