Identification of key components in the chemical and physical milieu for directing osteogenesis is a requirement in the investigation of tissue engineering scaffolds for advancement of bone regeneration. In this study, we engineered different gelatin-based cryogels and studied the effect of nanohydroxyapatite (nHAP) and crosslinking agents on scaffold properties and its osteogenic response towards bone marrow stem cells (BMSCs). The cryogels examined are 5% gelatin and 5% gelatin/2.5% nHAP, crosslinked either with 1-ethyl-3-(3-dimethylaminopropyl)-carbodiimide (EDC) or glutaraldehyde (GA). We confirmed that nHAP or the crosslinking agent has no effects on scaffold pore size and porosity. Nonetheless, incorporation of nHAP increased mechanical strength, swelling ratio and degree of crosslinking, but decreased degradation rate. Cryogels crosslinked with EDC showed faster degradation and promoted osteogenic differentiation of BMSCs while those prepared from GA crosslinking promoted proliferation of BMSCs. Furthermore, osteogenic differentiation was always enhanced in the presence of nHAP irrespective of the culture medium (normal or osteogenic) used but osteogenic medium always provide a higher extent of osteogenic differentiation. Employing gelatin/nHAP cryogel crosslinked by EDC in a bioreactor for dynamic culture of BMSCs, cyclic compressive mechanical simulation was found to be beneficial for both cell proliferation and osteogenic differentiation. However, the optimum conditions for osteogenic differentiation and cell proliferation were found at 30% and 60% strain, respectively. We thus demonstrated that osteogenic differentiation of BMSCs could be tuned by taking advantages of chemical cues generated from scaffold chemistry or physical cues generated from dynamic cell culture in vitro. Furthermore, by combining the best cryogel preparation and in vitro cell culture condition for osteogenesis, we successfully employed in vitro cultured cryogel/BMSCs constructs for repair of rabbit critical-sized cranial bone defects.
Download full-text PDF |
Source |
---|---|
http://dx.doi.org/10.1016/j.msec.2019.109855 | DOI Listing |
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!