Graphene Oxide and Oxidized Carbon Black as Catalyst for Crosslinking of Phenolic Resins.

Influence of different graphite-based nanofillers on crosslinking reaction of resorcinol, as induced by hexa(methoxymethyl)melamine, is studied. Curing reactions leading from low molecular mass compounds to crosslinked insoluble networks are studied by indirect methods based on Differential Scanning Calorimetry. Reported results show a catalytic activity of graphene oxide (eGO) on this reaction, comparable to that one already described in the literature for curing of benzoxazine. For instance, for an eGO content of 2 wt %, the exothermic crosslinking DSC peak (upon heating at 10 °C/min) shifted 6 °C. More relevantly, oxidized carbon black (oCB) is much more effective as catalyst of the considered curing reaction. In fact, for an oCB content of 2 wt %, the crosslinking DSC peak can be shifted more than 30 °C and a nearly complete crosslinking is already achieved by thermal treatment at 120 °C. The possible origin of the higher catalytic activity of oCB with respect to eGO is discussed.