Objective: Polymerization of light-cured resin-based materials is well documented; however, the intensity of the activating light can be reduced by passage through air, dental structure, or restoration compromising the physical properties of the restoration. The aim of this study was to evaluate the depth of cure of different light cured composite resins polymerized directly or transdental, through enamel and enamel/dentin tissues.
Material And Methods: Five composite resins were selected for this experiment: SureFil SDR, Dentsply (SDR), Filtek Supreme Plus, 3M ESPE (FSP), Aelite LS, Bisco (ALS), Filtek LS, 3M ESPE (FLS), and TPH, Dentsply (TPH). Thirty specimens of each material were prepared with 2- or 4-mm thickness. The specimens were light-cured (Elipar 2500, 3M ESPE) for 40 sec using three different protocols: direct or transdental, through a disc of enamel with 1 mm of thickness, and a disc of enamel and dentin with 2 mm of thickness. Eight Vickers microhardness (VH) measurements were taken from each specimen, four on top and four on bottom surface (Micromet, Buehler, 100 g per 15 sec). Data was analyzed with ANOVA three-way, Tukey HSD post-hoc (α = .05).
Results: Bottom surfaces of specimens exhibited statistically significant lower Vickers microhardness than the top surfaces for all composite resin evaluated, regardless of the curing conditions, except for the SDR when direct light-cured. Transdental light curing through enamel/dentin layer, significantly decreased VH (P<0.05) on the bottom surface of all composite groups.
Conclusion: The results of this study showed that light-curing attenuation of dental structures negatively affect the micro-hardness of composite resins.
Download full-text PDF |
Source |
|---|---|
| http://www.ncbi.nlm.nih.gov/pmc/articles/PMC6604562 | PMC |
| http://dx.doi.org/10.15644/asc53/2/1 | DOI Listing |
Publication Analysis
Top Keywords
Similar Publications
Gingival margin interfacial microleakage, staining, and push-out strengths of gingival colored composite resins in denture bases.
J Prosthet Dent
January 2025
Professor, Department of Dentistry, Federal University of Santa Catarina (UFSC), Florianópolis, SC, Brazil. Electronic address:
Statement Of Problem: Staining at the gingival margin could impact denture longevity, but the behavior of gingival colored composite resins (GCCs) in this area remains unclear.
Purpose: This in vitro study evaluated surface staining, microleakage, and push-out bond strength at the gingival margin of artificial teeth, comparing two consistencies of GCCs with two resin base materials.
Material And Methods: Specimens included artificial teeth (Ivostar; Ivoclar AG) and two acrylic resin base materials: conventional (Ondacryl; Clássico) and high-impact (Diamond D; Keystone Industries) (n=300).
The role of aging and various surface preparation methods in the repair of nanohybrid composites.
BMC Oral Health
January 2025
Faculty of Dentistry, Department of Restorative Dentistry, Gazi University, Bişkek St. 1. St. Number: 8 Emek, Ankara, Turkey.
Background: Repairing composite resins is a less invasive alternative to complete restoration replacement. To achieve a successful bond between the existing and newly applied composite materials, various surface preparation methods, such as sandblasting and acid etching, have been explored. The aim of the study was to evaluate the effect of different surface treatments on the repair bond strength of a universal nanohybrid composite resin restorative material before and after thermal aging, by utilizing a micro-shear bond strength (µSBS) test.
View Article and Find Full Text PDFSurface roughness of composite resins subjected to brushing with whitening toothpastes: an in vitro study.
Braz Oral Res
January 2025
Pontifícia Universidade Católica do Rio Grande do Sul - PUC-RS, School of Health and Life Sciences, Department of Pediatric Dentistry, Porto Alegre, RS, Brazil.
The emergence of toothpastes containing different abrasive and whitening substances has been a constant concern among dental professionals. The aim of the present study was to perform an in vitro assessment of the surface topography of nanoparticle composite resins subjected to simulated brushing with dentifrices. Test samples were prepared with Filtek Universal (3M ESPE), Filtek Bulkfill (3M ESPE) and Z350 (3M ESPE), with 24 samples per resin.
View Article and Find Full Text PDFHEMA-free versus HEMA-containing adhesive systems: a systematic review.
Syst Rev
January 2025
Conservative Dentistry Department, Faculty of Dentistry, Mansoura University, Mansoura, Postal Code, 35516, Egypt.
Background: Hydrophilic monomer 2-hydroxyethyl methacrylate (HEMA)-free adhesive systems are gaining increasing popularity nowadays. Although the addition of HEMA to dental adhesives improves dentin wettability and resin diffusion into demineralized collagen fibrils, HEMA's high hydrophilicity can lead to hydrolytic degradation of the adhesive interface. Thus, HEMA-free adhesive systems have been developed.
View Article and Find Full Text PDFDigitized thermo-responsive shape memory matrix band for tooth restorations.
Sci Rep
January 2025
Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Hangzhou, 310000, China.
Direct resin restoration has been widely used to restore the tooth defect for its convenience and minimal invasion. However, the accuracy of the final contour of class II restoration is often unpredictable and quite technique-sensitive due to the limitation of traditional matrix band system. In this study, the authors developed a novel matrix band system using shape memory polymer (SMP), which possessed two reversible shapes including digitized permanent shape to reproduce anatomical proximal contour and programmable temporary shape for clinical practice and reservation.
View Article and Find Full Text PDFWant AI Summaries of new PubMed Abstracts delivered to your In-box?
Enter search terms and have AI summaries delivered each week - change queries or unsubscribe any time!