Direct Growth of CNTs@CoS Se on Carbon Cloth for Overall Water Splitting.

Searching for low-cost, high-efficiency, bifunctional, non-noble-metal electrocatalysts for overall water splitting is crucial to renewable energy conversion. Herein, a series of component-controllable CC/CNTs@CoS Se (CC: carbon cloth, CNT: carbon nanotube) with excellent bifunctional properties in the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) were obtained by chemical vapor deposition. In this strategy, the Zif-67 precursor served as a structural inducer, which was directly grown on CC and pyrolyzed with the assistance of melamine to form multi-walled CNT-encapsulated CoS Se hierarchical nanostructures. Subsequently, the electrocatalytic properties of the as-prepared materials were optimized by adjusting the S/Se molar ratio. Of note is that the lattice distortion caused by the different radii of Se and S generated a polarized electric field for easy adsorption of the intermediate products. The CoOOH generated in situ on the surface of CoS Se , as well as n- and p-type domains in carbon, synergistically resulted in abundant active sites to boost the electrocatalytic activity. CC/CNTs@CoS Se exhibited overpotentials for the HER and OER of 225 and 285 mV, respectively and attained a current density of 10 mA cm in alkaline solution. The as-prepared electrocatalysts could act as both cathode and anode in a water electrolyzer showing a cell voltage of 1.74 V and delivering 10 mA cm , comparable to those of noble-metal-based water electrolyzers.