[Preparation and evaluation of carboxymethyl chitosan/sodium alginate hydrogel for cartilage tissue engineering].

Objective: This study aimed to optimize the preparation of carboxymethyl chitosan/sodium alginate (CMCS/OSA) compound hydrogels. This study also aimed to investigate the applicability of the hydrogels in cartilage tissue engi-neering.

Methods: Three groups of CMCS/OSA composite hydrogels with amino-to-aldehyde ratios of 2∶1, 1∶1 and 1∶2 were prepared. The microstructure, physical properties, and cell biocompatibility of the three groups of CMCS/OSA com-posite hydrogels were evaluated. Samples were subjected to scanning electron microscopy, rheological test, adhesion tension test, swelling rate test, and cell experiments to identify the CMCS/OSA composite hydrogel with the cross-linking degree that can meet the requirements for scaffolds in cartilage tissue engineering.

Results: The experimental results showed that the CMCS/OSA hydrogel with a amine-to-aldhyde ratio of 1∶1 had good porosity, suitable gelling time, strong adhesive force, stable swelling rate, and good cellular biocompatibility.

Conclusions: The CMCS/OSA compound hydrogel prepared with a 1∶1 ratio of amino and aldehyde groups has potential applications in cartilage tissue engineering.