Functionalization of MXene Nanosheets for Polystyrene towards High Thermal Stability and Flame Retardant Properties.

Fabricating high-performance MXene-based polymer nanocomposites is a huge challenge because of the poor dispersion and interfacial interaction of MXene nanosheets in the polymer matrix. To address the issue, MXene nanosheets were successfully exfoliated and subsequently modified by long-chain cationic agents with different chain lengths, i.e., decyltrimethylammonium bromide (DTAB), octadecyltrimethylammonium bromide (OTAB), and dihexadecyldimethylammonium bromide (DDAB). With the long-chain groups on their surface, modified TiC (MXene) nanosheets were well dispersed in ,-dimethylformamide (DMF), resulting in the formation of uniform dispersion and strong interfacial adhesion within a polystyrene (PS) matrix. The thermal stability properties of cationic modified TiC/PS nanocomposites were improved considerably with the temperatures at 5% weight loss increasing by 20 °C for DTAB-TiC/PS, 25 °C for OTAB-TiC/PS and 23 °C for DDAB-TiC/PS, respectively. The modified MXene nanosheets also enhanced the flame-retardant properties of PS. Compared to neat PS, the peak heat release rate (PHRR) was reduced by approximately 26.4%, 21.5% and 20.8% for PS/OTAB-TiC, PS/DDAB-TiC and PS/DTAB-TiC, respectively. Significant reductions in CO and CO productions were also obtained in the cone calorimeter test and generally lower pyrolysis volatile products were recorded by PS/OTAB-TiC compared to pristine PS. These property enhancements of PS nanocomposites are attributed to the superior dispersion, catalytic and barrier effects of TiC nanosheets.