Application of Response Surface Methodology and Desirability Function in the Optimization of Adsorptive Remediation of Arsenic from Acid Mine Drainage Using Magnetic Nanocomposite: Equilibrium Studies and Application to Real Samples.

A magnetic multi-walled carbon nanotube/zeolite nanocomposite was applied for the adsorption and removal of arsenic ions in simulated and real acid mine drainage samples. The adsorption mechanism was investigated using two-parameter (Langmuir, Freundlich, Temkin) and three-parameter (Redlich-Peterson, and Sips) isotherm models. This was done in order to determine the characteristic parameters of the adsorptive removal process. The results showed that the removal process was described by both mono- and multilayer adsorptions. Adsorption studies demonstrated that a multi-walled carbon nanotube/zeolite nanocomposite could efficiently remove arsenic in simulated samples within 35 min. Based on the Langmuir isotherm, the adsorption capacity for arsenic was found to be 28 mg g. The nanocomposite was easily separated from the sample solution using an external magnet and the regeneration was achieved by washing the adsorbent with 0.05 mol L hydrochloric acid solution. Moreover, the nanoadsorbent was reusable for at least 10 cycles of adsorption-desorption with no significant decrease in the adsorption capacity. The nanoadsorbent was also used for the arsenic removal from acid mine drainage. Overall, the adsorbent displayed excellent reusability and stability; thus, they are promising nanoadsorbents for the removal of arsenic from acid mine drainage.